Описание материалов:
DOW LDPE™132G low density polyethylene resin can be easily extruded by commonly used blown film technology, and the melt temperature range used is 170 to 230°C. At the time of preparation, this resin combines processability, stiffness and physical properties well. This product does not contain slip agent or opening agent.
Remarks: Comply with the following regulations:
U.S. Food and Drug Administration Regulation 21 CFR 177.1520(c)2.2
EU, No 10/2011
Please inquire regulations for complete details
Application fields:
Remarks: Comply with the following regulations:
U.S. Food and Drug Administration Regulation 21 CFR 177.1520(c)2.2
EU, No 10/2011
Please inquire regulations for complete details
Application fields:
- Heavy packaging industrial film
- shrink film
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.921 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 51 | µm | |
| Прочность пленки | ASTM D882 | ||
| MD : 51 µm | 216 | J/cm³ | ASTM D882 |
| TD : 51 µm | 211 | J/cm³ | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 31.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 28.9 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 51 µm | 470 | % | ASTM D882 |
| TD : Fracture, 51 µm | 660 | % | ASTM D882 |
| Ударное падение Dart (51 µm) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 300 | g | ASTM D1922 |
| TD : 51 µm | 180 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.8 µm) | 50 | ASTM D2457 | |
| Haze (50.8 µm) | 11 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 216 | °C |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.02 mm) 熔体温度：420°F (215°C) 输出：模具周长的 8 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Westlake LDPE EP310 | LDPE | Westlake Chemical Corporation |
| Westlake LDPE EC1924AA | LDPE | Westlake Chemical Corporation |
| 陶氏低密度聚乙烯 600C | LDPE | The Dow Chemical Company |
| ASI POLYETHYLENE CP 795-01 Natural | LDPE | A. Schulman Inc. |
| OKITEN® 222 A | LDPE | DIOKI d.d. |
| Osterlene® LDC1821A | LDPE | Osterman & Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved