Описание материалов:
Lustran ABS LGA resin is a low-gloss grade of ABS (acrylonitrile butadiene styrene). This automotive injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance. The resin is available in natural and black colors only. The consistent, clean, natural color of LGA makes it ideally suitable for use with color concentrates.
Lustran ABS LGA resin is designed to meet stringent physical property and appearance requirements for low-loss automotive interior trim applications. Typical uses are pillar posts, consoles, scuff plates, map pockets, and interior quarter trim panels. As with any product, use of Lustran ABS LGA resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Глянец, низкий
- Хорошая ударопрочность
|
| Используется | - Применение в автомобильной области
- Автомобильные внутренние детали
|
| Рейтинг агентства | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Многоточечные данные | - Изохронный стресс против деформации (ISO 11403-1)
- Изоляционный стресс против деформации (ISO 11403-1)
- Сектантный модуль против деформации (ISO 11403-1)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.05 | g/cm³ | ASTM D792 |
| Удельный объем | 0.950 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 220°C/10.0 kg | 21 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 - 0.70 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 105 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2210 | MPa | ASTM D638 |
| Прочность на растяжение | | | |
| Yield | 36.5 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2 |
| Флекторный модуль | | | |
| -- | 2410 | MPa | ASTM D790 |
| -- | 2430 | MPa | ISO 178 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| -40°C 1 | 7.7 | kJ/m² | ISO 180/1A |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, 3.18mm | 90.0 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 92.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 100 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 76.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| Викат Температура размягчения | | | |
| -- | 107 | °C | ASTM D1525 3 |
| -- | 96.0 | °C | ISO 306/B50 |
| CLTE-
Поток (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.57 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость горения 4 | 53 | mm/min | SAE J1685 |
| Огнестойкость | | | UL 94 |
| 1.57 mm | HB | | UL 94 |
| 3.18 mm | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | | | |
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Время сушки | | | |
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.10 | % | |
| Рекомендуемый размер снимка | 50 - 75 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 235 - 249 | °C | |
| Средняя температура | 241 - 254 | °C | |
| Передняя температура | 246 - 260 | °C | |
| Температура сопла | 246 - 260 | °C | |
| Температура обработки (расплава) | 246 - 266 | °C | |
| Температура формы | 43.3 - 65.6 | °C | |
| Давление впрыска | 68.9 - 110 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Тонаж зажима | 2.8 - 5.5 | kN/cm² | |
| Подушка | < 6.35 | mm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Примечание |
|---|
| 1 . | 4x10 mm bar |
| 2 . | 4x10 mm bar |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| 4 . | 2x100x355 mm |