Описание материалов:
Jamplast ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.
The sheet and thermoforming grades of Jamplast ABS resins provide excellent high and low gloss aesthetics, thermal color stability, heat and impact resistance and stiffness for applications such as luggage, tool cases, burial vault liners, signs and recreation vehicles. Jamplast ABS resins can fill a variety of needs by offering ranges in melt flow rates from 1.0 to 4.0 g/10 min., sheet Izod impacts from 2.5 to 10.5 ft-lb/in and sheet flexural modulus from 285,000 to 300,000 psi.
This resin is the lowest gloss and highest melt flow rate option of our ABS sheet grades. With a melt flow rate of 4.0 g/10 min., JPLGABSE can be used for low gloss, low impact applications where easy processability is desired.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | - Литье под давлением
- Экструзионный профиль
- Экструзионный лист
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/3.8 kg) | 3.9 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 to 0.70 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| L-Scale | 80 | | |
| R-Scale | 108 | | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 1860 | MPa | ASTM D638 |
| Прочность на растяжение 2 | | | ASTM D638 |
| Yield | 30.3 | MPa | |
| Break | 31.7 | MPa | |
| Удлинение при растяжении 3(Break) | 50 | % | ASTM D638 |
| Флекторный модуль 4 | 2210 | MPa | ASTM D790 |
| Flexural Strength 5 | 62.1 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -18°C, 3.18 mm 6 | 80 | J/m | |
| 23°C, 3.18 mm 7 | 130 | J/m | |
| Gardner Impact | | | ASTM D3029 |
| -18°C, 2.54 mm | 19.8 | J | |
| 23°C, 2.54 mm | 22.6 | J | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed, 3.18 mm) | 96.1 | °C | ASTM D648 |
| Викат Температура размягчения | 104 | °C | ASTM D1525 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (1.52 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 to 87.8 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.10 | % | |
| Температура обработки (расплава) | 218 to 274 | °C | |
| Температура формы | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Тонаж зажима | 2.8 to 6.9 | kN/cm² | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 1.5:1.0 to 3.5:1.0 | | |
| Примечание |
|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 2.5E-3 mm Notch Depth |