Описание материалов:
Nylon is one of the most widely used and versatile thermoplastic resins. Its combination of physical properties versus its price makes it a favorite choice for numerous applications. Nylon has a consistent history of replacing other materials including: metal, brass, bronze, aluminum, and rubber. In replacing metal gears in machinery, nylon can be advantageous because of its ability to reduce noise, use less lubrication and increase gear life. TECAMID® MDS is an extruded "moly" filled nylon 6/6, which is gray in color. The addition of particles of molybdenum disulfide enhances the surface lubricity and wear resistance over unfilled nylon. In applications requiring high lubricity, this material may be a good candidate. In addition to the greater lubricity there are many additional property enhancementsthat occur.
TECAMID® MDS has enhanced properties which make it an ideal material to replace metals in machinery. It can increase the life of many moving parts as well as provide a noise reduction benefit and requires less lubrication. A very stable compound with many industrial applications.
| Главная Информация | |
|---|
| Добавка | - Смазка дисульфида молибдена
|
| Характеристики | - Низкий коэффициент трения
- Смазка
|
| Используется | - Промышленное применение
- Замена металла
|
| Внешний вид | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.14 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 23°C, 24 hr | 1.2 - 2.5 | % | ASTM D570 |
| Saturated, 23°C | 7.5 - 8.5 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (M-Scale, 23°C) | 87 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3100 | MPa | ASTM D638 |
| Прочность на растяжение (Yield, 23°C) | 75.8 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 23°C) | 15 | % | ASTM D638 |
| Флекторный модуль (23°C) | 3100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 117 | MPa | ASTM D790 |
| Коэффициент износа 1(0.28 MPa, 0.25 m/sec) | 380 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Незубчатый изод Impact (23°C) | 64 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 243 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648 |
| Пиковая температура плавления | 255 | °C | ASTM D3418 |
| CLTE-
Поток | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Удельный нагрев | 1670 | J/kg/°C | |
| Максимальная температура обслуживания | | | |
| Intermittent | 179 | °C | |
| Long Term | 110 | °C | UL 746B |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | 1.0E+15 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность | 1.2 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная 2(23°C, 60 Hz) | 2.50 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | HB | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from extruded shapes material. |
| Примечание |
|---|
| 1 . | Against Steel |
| 2 . | 50% RH |