Описание материалов:
Vydyne R525H Nat is high-flow, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R525H Nat is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R525H Nat has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses
To come
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 25% наполнитель по весу
|
| Добавка | |
| Характеристики | - Антифриз устойчивый
- Устойчивость к усталости
- Сопротивление бензину
- Хорошая химическая стойкость
- Стабилизация тепла
- Высокий поток
- Смазка
- Устойчивость к растворителям
|
| Используется | - Автомобильная крышка под капот
|
| Рейтинг агентства | - Астм д 4066 PA0121G25
- Астм д 6779 PA0121G25
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.32 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow
: 23°C, 2.00 mm | 0.40 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 0.90 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 8600 | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 174 | 117 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, 23°C) | 3.0 | 7.0 | % | ISO 527-2 |
| Флекторный модуль (23°C) | 7700 | 5700 | MPa | ISO 178 |
| Флекторный стресс (23°C) | 250 | 150 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | | ISO 527-2 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179/1eA |
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 11 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179/1eU |
| -30°C | 55 | 66 | kJ/m² | |
| 23°C | 65 | 67 | kJ/m² | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -30°C | 9.0 | 10 | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 2.5E-5 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 140 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 140 | -- | °C | |
| 3.00 mm | 140 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление (3.00 mm) | PLC 6 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 250 to 399 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 1 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 3 | -- | | |
| 3.00 mm | PLC 4 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| Индекс воспламеняемости провода свечения | | | | IEC 60695-2-12 |
| 0.750 mm | 675 | -- | °C | |
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| Температура зажигания провода свечения | | | | IEC 60695-2-13 |
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Дополнительная информация | Сухой | Состояние | | Метод испытания |
|---|
| Automotive Materials -
(thickness d = 1mm) | + | -- | | FMVSS 302 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 280 to 310 | °C | |
| Средняя температура | 280 to 310 | °C | |
| Передняя температура | 280 to 310 | °C | |
| Температура сопла | 280 to 310 | °C | |
| Температура обработки (расплава) | 285 to 305 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |