Описание материалов:
Provides wide range moldability and Superior cost performance and Expands the possibility of design.
Kyocera Chemical's Phenolic Molding Compounds "TECOLITE" can possible to high cycle molding and excellent stability within a cylinder. Moreover, "TECOLITE" have a wide molding condition and can be found out easily. In the parts, "TECOLITE" have small mold shrinkage factor therefore it is suitable for precision parts. It is especially the best for mass-production parts, such as a non-fuse breaker, various electric parts, and kitchen parts, etc.
| Главная Информация | |
|---|
| Характеристики | - Быстрое лечение
- Низкая усадка
|
| Используется | - Электрическое/электронное применение
- Кухонные принадлежности
|
| Внешний вид | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| Удельный вес | 1.43 | g/cm³ | |
| Формовочная усадка | | | |
| Flow 1 | 1.2 to 1.4 | % | |
| Flow 2 | 0.70 to 0.90 | % | |
| Across Flow 3 | 0.90 to 1.1 | % | |
| Поглощение воды (Equilibrium) | < 0.35 | % | |
| Механические | Номинальное значение | Единица измерения | |
|---|
| Flexural Strength | 78.0 to 98.0 | MPa | |
| Прочность на сжатие | 216 to 245 | MPa | |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Heat Deflection Temperature | 170 | °C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Insulation Resistance | | | |
| After Boiling | 1.0E+8 to 1.0E+9 | ohms | |
| As Molded | 1.0E+9 to 1.0E+11 | ohms | |
| Диэлектрическая прочность | > 8.0 | kV/mm | |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (0.510 mm) | HB | | UL 94 |
| Примечание |
|---|
| 1 . | Injection Molding |
| 2 . | Compression Molding |
| 3 . | Injection Molding |