Описание материалов:
Eastman is pleased to announce the launch of DRYSTAR* copolyesters. This new product-line is designed to meet the needs of converters seeking value-added solutions to their drying requirements of copolyesters. Eastman?s copolyesters are highly valued for their excellent balance of properties such as superior aesthetics, impact strength, and chemical resistance. These properties can be optimally realized when the resins are properly dehydrated in accordance to recommended drying conditions and equipment.
Recognizing this value, Eastman conceived Drystar™ copolyesters to allow converters with limited access to desiccant dryers to achieve these optimizations. In addition, some converters with desiccant dryers may still find Drystar™ copolyesters value-adding to attain production flexibility and cost saving by removing the drying process prior to injection molding, profile extruding, or extrusion blow molding copolyesters. The initial launch comprises of the commercialization of four grades of Drystar™ copolyesters and Eastman has on-going program to extend this strategic product-line in the future.
*DRYSTAR is only available in the Asia Pacific Region.
| Главная Информация | |
|---|
| Характеристики | - Хорошая химическая стойкость
- Хорошая ударопрочность
- Приятный внешний вид
|
| Формы | |
| Метод обработки | - Экструзионное выдувное формование
- Литье под давлением
- Экструзионный профиль
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.27 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 108 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 23°C | 2030 | MPa | ASTM D638 |
| 23°C | 2000 | MPa | ISO 527-2 |
| Прочность на растяжение | | | |
| Yield, 23°C | 50.0 | MPa | ASTM D638 |
| Yield, 23°C | 48.0 | MPa | ISO 527-2 |
| Break, 23°C | 30.0 | MPa | ASTM D638 |
| Break, 23°C | 29.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C | 4.4 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 180 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 2060 | MPa | ASTM D790 |
| 23°C | 2100 | MPa | ISO 178 |
| Flexural Strength | | | |
| 23°C | 68.0 | MPa | ASTM D790 |
| 23°C | 67.0 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -40°C | 4.4 | kJ/m² | ISO 180 |
| 23°C | 9.4 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4812 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | °C | ASTM D648, ISO 75-2/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания | 90.0 | % | ASTM D1003 |
| Haze | 0.20 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.0 | °C | |
| Время сушки | 6.0 | hr | |
| Температура обработки (расплава) | 249 to 271 | °C | |
| Температура формы | 16.0 to 38.0 | °C | |