- AGILITY™ 1000 Performance LDPE
AGILITY™ 1000 Performance LDPE
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | AGILITY™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
5SkvCY_AGILITY-1000-Performance-LDPE.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
AGILITY™ 1000 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability. AGILITY™ 1000 Performance LDPE also has excellent shrink and good optics performance in blends with LLDPE resins.
Main Characteristics:
Complies with:
Main Characteristics:
- Faster processing LDPE resin
- Designed for higher output rates in blends with LLDPE resins
- Excellent shrink
Complies with:
- U.S. FDA, 21 CFR 177.1520(c)2.2
- Canadian HPFB No Objection
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.920 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.18 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 51 | µm | |
| Сопротивление проколу пленки (51 µm) | 6.04 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 51 µm | 221 | MPa | ASTM D882 |
| 2% secant, MD : 51 µm | 200 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm | 254 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 225 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 51 µm | 12.4 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.7 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 28.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 26.8 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 51 µm | 390 | % | ASTM D882 |
| TD : Fracture, 51 µm | 560 | % | ASTM D882 |
| Ударное падение Dart (51 µm) | 270 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 180 | g | ASTM D1922 |
| TD : 51 µm | 200 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления (DSC) | 109 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.8 µm) | 61 | ASTM D2457 | |
| Четкость (50.8 µm) | 92.0 | ASTM D1746 | |
| Haze (50.8 µm) | 10 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. (88.9 mm), 30:1 L/D Die Gap: 30 mil (1.78mm) Melt Temperature: 423°F (217°C) Output: 10 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 45.3 rpm Frost Line Height: 31 in. (787 mm) |
| Примечание | |
|---|---|
| 1 . | Method B |
| Тип материала | Категория | Производитель |
|---|---|---|
| SABIC® LDPE 2001TX17 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| MTEGRITY™ LDPE LD225AA | LDPE | M. Holland Company |
| VENELENE® FB-7000 | LDPE | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark PE LD2923B | LDPE | Trademark Plastics Corporation |
| 陶氏低密度聚乙烯 440C | LDPE | The Dow Chemical Company |
| InnoPlus LD2026K | LDPE | PTT Global Chemical Public Company Limited |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved