Описание материалов:
Lustran ABS 752 resin is a high-gloss, high-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). In its natural color (000000), Lustran ABS 752 meets FDA requirements for food contact.** It also provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates.
Lustran ABS 752 resin is used for extrusion applications that require high-impact toughness. Typical applications include various carrying cases, table tops, wall panels, and profiles. It is also used as a substrate under other specialty grades, such as Lustran ABS 556 low-gloss resin. As with any product, use of Lustran ABS 752 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Подсветка
- Высокая стабильность расплава
- Высокая ударопрочность
- Хорошая окраска
- Хорошая прочность
|
| Используется | - Мебель
- Стеновая панель
- Профиль
|
| Рейтинг агентства | - EC 1907/2006 (REACH)
- FDA пищевой контакт, не Номинальный
|
| Внешний вид | - Доступные цвета
- Натуральный цвет
|
| Формы | |
| Метод обработки | - Экструзия
- Термоформовка
- Экструзионное формование профиля
|
| Многоточечные данные | - Изоляционный стресс против деформации (ISO 11403-1)
- Сектантный модуль против деформации (ISO 11403-1)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792 |
| Удельный объем | 0.960 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 230°C/10.0 kg | 7.7 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 1.7 | g/10 min | ASTM D1238 |
| Поглощение воды (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 102 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ASTM D638 |
| -18°C | 2070 | MPa | ASTM D638 |
| 23°C | 1860 | MPa | ASTM D638 |
| 71°C | 1310 | MPa | ASTM D638 |
| Прочность на растяжение | | | ASTM D638 |
| Yield, -18°C | 51.0 | MPa | ASTM D638 |
| Yield, 23°C | 35.2 | MPa | ASTM D638 |
| Yield, 71°C | 19.3 | MPa | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -40°C | 2410 | MPa | ASTM D790 |
| 23°C | 1860 | MPa | ASTM D790 |
| 71°C | 1520 | MPa | ASTM D790 |
| Flexural Strength | | | ASTM D790 |
| Yield, -40°C | 89.6 | MPa | ASTM D790 |
| Yield, 23°C | 55.2 | MPa | ASTM D790 |
| Yield, 71°C | 41.4 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C, 3.18 mm | 180 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 240 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 370 | J/m | ASTM D256 |
| Ударное устройство для дротиков | | | ASTM D3763 |
| -40°C, Peak Energy | 28.5 | J | ASTM D3763 |
| -40°C, 3.18 mm, Total Energy | 31.2 | J | ASTM D3763 |
| -18°C, Peak Energy | 31.2 | J | ASTM D3763 |
| -18°C, Total Energy | 40.7 | J | ASTM D3763 |
| 23°C, Peak Energy | 27.1 | J | ASTM D3763 |
| 23°C, Total Energy | 46.1 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 98.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 92.2 | °C | ASTM D648 |
| CLTE-
Поток | 9.4E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (0.762 mm) | 60.0 | °C | UL 746 |
| RTI Imp (0.762 mm) | 60.0 | °C | UL 746 |
| RTI Str (0.762 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость горения 1(3.18 mm) | 36 | mm/min | ASTM D635 |
| Огнестойкость (1.50 mm) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60 °, extruded sheet) | 90 | | ASTM D523 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 - 93.3 | °C | |
| Время сушки | 3.0 - 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.030 | % | |
| Зона цилиндра 1 темп. | 216 - 241 | °C | |
| Зона цилиндра 2 температура. | 218 - 241 | °C | |
| Зона цилиндра 3 темп. | 218 - 241 | °C | |
| Зона цилиндра 4 темп. | 218 - 241 | °C | |
| Зона цилиндра 5 темп. | 218 - 241 | °C | |
| Температура расплава | 216 - 249 | °C | |
| Температура матрицы | 210 - 241 | °C | |
| Рулон для снятия | 62.8 - 104 | °C | |
| Инструкции по экструзии |
|---|
| Max. Regrind Allowed: 40% |
| Примечание |
|---|
| 1 . | Injection Molded specimen |