SABIC® SUPEER™ 8118
| Категория | mLLDPE, Metallocene Linear Low Density Polyethylene |
| Производитель | Saudi Basic Industries Corporation (SABIC) |
| Торговая марка | SABIC® SUPEER™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
4s9oLH_SABICSUPEER8118.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
SABIC® SUPEER™ 8118 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity.
Application
Typical applications for SABIC® SUPEER™ 8118 are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
Application
Typical applications for SABIC® SUPEER™ 8118 are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.918 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 140 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 156 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 54.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 54.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 630 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Ударное падение Dart 1(50 µm, Blown Film) | 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 14 | g | ASTM D1922 |
| TD : 50 µm, blown film | 22 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления | 115 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Примечание | |
|---|---|
| 1 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| PRIMALENE WPP692M | mLLDPE | Southern Polymer, Inc. |
| Trademark PE mLLD1918B | mLLDPE | Trademark Plastics Corporation |
| Eltex® PF6912AA | mLLDPE | INEOS Olefins & Polymers Europe |
| Daelim Po1y® XP5400 | mLLDPE | DAELIM INDUSTRIAL CO., LTD. |
| Eltex® PF6212LA | mLLDPE | INEOS Olefins & Polymers Europe |
| Daelim Po1y® XP9200N | mLLDPE | DAELIM INDUSTRIAL CO., LTD. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved