Описание материалов:
TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp.
In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles.
TROGAMID® BX9724
Polymer blend consisting of amorphous and semi-crystalline polyamides, 40% glass fiber reinforced, with high tensile modulus for injection molding, dimensionally stable even while absorbing water; appropriate for substituting cast metal parts with plastic. Moldings exhibit outstanding surface qualities in spite of their high glass fiber content.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 40% наполнитель по весу
|
| Характеристики | - Аморфный
- Сополимер
- Хорошая химическая стойкость
- Хорошая стабильность размеров
- Хорошие электрические свойства
- Хорошая термическая стабильность
- Высокая вязкость
- Низкая усадка
- Низкий уровень защиты
- Выдающаяся поверхность
- Полукристаллический
|
| Используется | - Электрическое/электронное применение
- Фильтры
- Шестерни
- Машина/механические детали
- Замена металла
|
| Внешний вид | - Прозрачный/прозрачный
- Доступные цвета
- Натуральный цвет
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.48 | g/cm³ | ISO 1183 |
| Номер вязкости | 130 | cm³/g | ISO 307 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше (Shore D) | 90 | | ISO 868 |
| Твердость мяча | 262 | MPa | ISO 2039-1 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 220 | MPa | ISO 527-2/5 |
| Номинальное растяжение при разрыве | 3.2 | % | ISO 527-2/5 |
| Растяжимый ползучий модуль | | | ISO 899-1 |
| 1 hr | 9600 | MPa | |
| 1000 hr | 5200 | MPa | |
| Флекторный модуль | 12000 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| -30°C, Complete Break | 10 | kJ/m² | |
| 0°C, Complete Break | 11 | kJ/m² | |
| 23°C, Complete Break | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | ISO 179/1eU |
| -30°C, Complete Break | 80 | kJ/m² | |
| 0°C, Complete Break | 87 | kJ/m² | |
| 23°C, Complete Break | 96 | kJ/m² | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 230 | °C | ISO 75-2/B |
| Температура перехода стекла 1 | 93.0 | °C | ISO 11357-2 |
| Викат Температура размягчения | 230 | °C | ISO 306/B |
| Температура плавления (DSC) | 260 | °C | ISO 3146 |
| CLTE | | | ISO 11359-2 |
| Flow
: 23 to 80°C | 2.2E-5 | cm/cm/°C | |
| Transverse
: 23 to 80°C | 3.8E-5 | cm/cm/°C | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+13 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Электрическая прочность | 27 | kV/mm | IEC 60243-1 |
| Относительная проницаемость (23°C, 1 MHz) | 6.20 | | IEC 60250 |
| Коэффициент рассеивания (23°C, 1 MHz) | 0.025 | | IEC 60250 |
| Comparative Tracking Index | | | IEC 60112 |
| -- 2 | 575 | V | |
| Solution A | 600 | V | |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 0.800 mm | HB | | |
| 1.60 mm | HB | | |
| Индекс воспламеняемости провода свечения (1.00 mm) | 750 | °C | IEC 60695-2-12 |
| Температура зажигания провода свечения (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Примечание |
|---|
| 1 . | 10 K/min |
| 2 . | 100 drops value |