MXSTEN® CV77519
| Категория | Plastic, Ethylene-based Plastomer , Plastomer |
| Производитель | Westlake Chemical Corporation |
| Торговая марка | MXSTEN® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
3uZBnv_MXSTEN-CV77519.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
CV77519 is a polyethylene plastomer designed for blown film extrusion that contains no slip or antiblock,and high processing aid additives. Films produced with this resin exhibit exceptionally low seal initiation temperature with a broad hot tack window combined with good stiffness. Other features of this resin include extreme strength in cold and refrigerated temperature environments, high resistance to tears, and high MVTR.
Application/Uses:
Agricultural tubing
Blown film
Food packaging
Application/Uses:
Agricultural tubing
Blown film
Food packaging
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.906 | g/cm³ | ASTM D4883 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 124 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 145 | MPa | ASTM D882 |
| Прочность на растяжение 2 | ASTM D882 | ||
| TD : Yield, 25 µm, blown film | 8.00 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 62.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 45.0 | MPa | ASTM D882 |
| Удлинение при растяжении 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1000 | % | ASTM D882 |
| Ударное падение Dart 4(25 µm, Blown Film) | > 2000 | g | ASTM D1709 |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, blown film | 600 | g | ASTM D1922 |
| TD : 25 µm, blown film | 650 | g | ASTM D1922 |
| Температура инициализации уплотнения 6(25 µm, Blown Film) | 82.0 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 25.4 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 6" die, 2.5":24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 450° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Примечание | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| 6 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Тип материала | Категория | Производитель |
|---|---|---|
| Exact™ 4049 | Plastomer | ExxonMobil Chemical |
| REVOLVE® M-687 | Plastomer | Matrix Polymers |
| Daelim Po1y® VL0001EN | Plastomer | DAELIM INDUSTRIAL CO., LTD. |
| Queo™ 0207LA | Plastomer | Borealis AG |
| REVOLVE® N-266 | Plastomer | Matrix Polymers |
| MXSTEN® CV77518 | Plastomer | Westlake Chemical Corporation |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved