Описание материалов:
Jamplast high gloss resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. Jamplast ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.
Jamplast ABS resins are designed to offer a wide range of impact strengths and melt flow rates to meet the needs of the durables injection molding markets. This product offers typical Izod impact strength values from 4 to 7.5 ft-lb/in and melt flow rates ranging from 2.5 to 7.0 g/10 min. The gloss values are typically greater than 95% on the 60° Gardner scale for the highest gloss resins and greater than 90% for those products having a broader range of gloss.
Jamplast ABS resin offers a broader range of gloss while maintaining medium impact strength with a medium melt flow rate.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 0.40 to 0.70 | % | ASTM D955 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 2240 | MPa | ASTM D638 |
| Прочность на растяжение 2 | | | ASTM D638 |
| Yield | 44.8 | MPa | |
| Break | 31.0 | MPa | |
| Удлинение при растяжении 3(Break) | 40 | % | ASTM D638 |
| Флекторный модуль 4 | 2550 | MPa | ASTM D790 |
| Flexural Strength 5 | 75.8 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact 6 | | | ASTM D256 |
| -18°C, 3.18 mm | 130 | J/m | |
| 23°C, 3.18 mm | 320 | J/m | |
| Ударное устройство для дротиков 7 | | | ASTM D3763 |
| -18°C, 3.18 mm, Peak Energy | 26.0 | J | |
| -18°C, 3.18 mm, Total Energy | 31.6 | J | |
| 23°C, 3.18 mm, Peak Energy | 33.9 | J | |
| 23°C, 3.18 mm, Total Energy | 55.4 | J | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed, 3.18 mm | 92.2 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 76.7 | °C | |
| Викат Температура размягчения | 106 | °C | ASTM D1525 |
| CLTE-
Поток | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (1.47 mm) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60°) | 90 | | ASTM D523 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 to 87.8 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.10 | % | |
| Температура обработки (расплава) | 218 to 274 | °C | |
| Температура формы | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 3.45 | MPa | |
| Тонаж зажима | 2.8 to 6.9 | kN/cm² | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 1.5:1.0 to 3.5:1.0 | | |
| Примечание |
|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| 7 . | 3.39 m/sec |