Описание материалов:
Bayflex LSR 10 is a solid elastomer which has a flexural modulus of 17,500 psi at room temperature. It is processed on reaction injection molding (RIM) equipment and is used for glass encapsulation of windows. This system combines rapid demold times, excellent integrity at demold, and outstanding physical properties.
The Bayflex LSR 10 system was developed to add a weather-resistant grade to our range of window encapsulation systems. In some cases, the weatherability of this system eliminates the need for post-painting or in-mold coatings. This product is available only in black. Bayflex LSR 10 is a formulated RIM system supplied as two reactive liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and component B is a polyether polyol. As with any product, use of the Bayflex LSR 10 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | |
|---|
| Плотность | 1.03 | g/cm³ | |
| Вязкость | | | |
| 25°C 1 | 100 | mPa·s | |
| 25°C 2 | 1320 | mPa·s | |
| Старение | Номинальное значение | | Метод испытания |
|---|
| Выдержка атмосферометра-
Дельта е 3 | 1.70 | | SAE J2527 |
| Воспламеняемость | Номинальное значение | Единица измерения | |
|---|
| Точка вспышки | | | |
| -- 4 | > 93 | °C | |
| -- 5 | > 121 | °C | |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Аризона выветривание-
Дельта е 6 | 0.350 | | GM 9327P |
| Флоридская погода-
Дельта е 7 | 1.70 | | GM 9327P |
| Дуга углерода солнечного света-
Дельта е 8 | 1.30 | | |
| Твердость | Номинальное значение | Единица измерения | |
|---|
| Твердость дюрометра | | | |
| Shaw A, 1 sec | 94 | | |
| Shaw A, 5 seconds | 93 | | |
| Shaw D, 1 sec | 44 | | |
| Shaw D, 5 seconds | 42 | | |
| Механические | Номинальное значение | Единица измерения | |
|---|
| Прочность на растяжение | 14.1 | MPa | |
| Удлинение при растяжении (Break) | 200 | % | |
| Флекторный модуль | | | |
| -30°C | 309 | MPa | |
| 25°C | 121 | MPa | |
| 70°C | 15.7 | MPa | |
| Эластомеры | Номинальное значение | Единица измерения | |
|---|
| Tear Strength 9 | 40.3 | kN/m | |
| Комплект сжатия 10 | 67 | % | |
| Термокомплект | Номинальное значение | | Метод испытания |
|---|
| Компоненты термокомплекта | | | |
| Component a 11 | Mixing ratio by weight: 54 | | |
| Component B 12 | Mixing ratio by weight: 100 | | |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Part A
Type: Isocyanate
Specific Gravity @ 25°C: 1.07
Viscosity @25°C: 100 mPa-s
Flash Point PMCC: >93.3 °C
Part B
Type: Polyol
Specific Gravity @ 25°C: 1.03
Viscosity @25°C: 1320 mPa-s
Flash Point PMCC: >121 °C |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 80.0 - 100 | °C | |
| Инструкции по впрыску |
|---|
| Polyol Temperature: 48 to 55°CIsocyanate Temperature: 40 to 46°CPolyol Nucleation: 0.9 to 1.00 S.G.Typical Cure Time at 0.125 in: 30 secMachine Reactivity at 40°C, Gel Time: 8 sec |
| Примечание |
|---|
| 1 . | Component A (Isocyanate) |
| 2 . | Component B (Polyol) |
| 3 . | 2500 kJ/m², Atlas CXW Open Flame, ASTM G155, Cycle 7 |
| 4 . | Component A (Isocyanate), PMCC |
| 5 . | Component B (Polyol), PMCC |
| 6 . | 2 years |
| 7 . | 2 years |
| 8 . | 1000 hr |
| 9 . | C mould |
| 10 . | 25% Deflection |
| 11 . | Isocyanate |
| 12 . | Polyol |