TOTAL Polypropylene PPH 4026
Описание материалов:
Polypropylene PPH 4026 is a homopolymer with a Melt Flow Index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.
Polypropylene PPH 4026 is intended for applications like hot fill food packaging, labeling, twist or lamination films.
Polypropylene PPH 4026 is a polypropylene homopolymer specifically developed to offer outstanding process ability for sheet extrusion and thermoforming applications.
Polypropylene PPH 4026 is characterized by a higher stiffness than conventional nucleated homopolymers, a good impact resistance and an excellent clarity. Polypropylene PPH 4026 allows for wall thickness reduction while maintaining appropriate top load and crush resistances.
Polypropylene PPH 4026 has excellent organoleptic properties making it suitable for the most sensitive packaging application.
| Главная Информация | |
|---|
| Характеристики | - Хорошая ударопрочность
- Хорошие органолептические свойства
- Хорошая технологичность
- Высокая четкость
- Высокая термостойкость
- Высокая жесткость
- Гомополимер
|
| Используется | - Пленка
- Этикетки
- Ламинаты
- Упаковка
- Лист
|
| Рейтинг агентства | |
| Соответствие RoHS | |
| Метод обработки | - Литая пленка
- Экструзионный лист
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.905 | g/cm³ | ISO 1183 |
| Видимая плотность | 0.53 | g/cm³ | ISO 60 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 95 | | ISO 2039-2 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2050 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 39.0 | MPa | ISO 527-2 |
| Растяжимое напряжение (Yield) | 9.0 | % | ISO 527-2 |
| Флекторный модуль | 2000 | MPa | ISO 178 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 50 | µm | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 50 µm, Cast Film | 31.0 | MPa | |
| TD
: Yield, 50 µm, Cast Film | 29.0 | MPa | |
| MD
: Break, 50 µm, Cast Film | 62.0 | MPa | |
| TD
: Break, 50 µm, Cast Film | 35.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 50 µm, Cast Film | 470 | % | |
| TD
: Break, 50 µm, Cast Film | 580 | % | |
| Ударное падение Dart (50 µm, Cast Film) | 80 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 50.0 µm | 6.0 | kN/m | |
| TD
: 50.0 µm | 88.0 | kN/m | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (23°C) | 6.0 | kJ/m² | ISO 179 |
| Зубчатый изод ударная прочность (23°C) | 5.0 | kJ/m² | ISO 180 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | | | |
| -- | 153 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| Температура плавления (DSC) | 165 | °C | ISO 3146 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 50.0 µm, Cast Film) | 51 | | ASTM D2457 |
| Haze (50.0 µm, Cast Film) | 14 | % | ISO 14782 |