Описание материалов:
SABIC® PP FPC55 is a grade developed for the thin wall packaging market. The grade is nucleated and is characterised by excellent flow behaviour in combination with an improved stiffness to impact balance. SABIC® PP FPC55 allows for very cost efficient processing on the basis of easy mould filling, short cycle times and improved part consistency in combination with pigments. It contains an antistatic package.
SABIC® PP FPC55 is typically used in thin wall packing applications both for food and non-food segments. This includes pails & containers, yellow fats/margarine tubs and dairy cups. In de caps and closure segment, the grade could be used for thin walled spray through caps, amongst other. The grade has excellent heat deflection temperature making it particularly suitable for hot fill applications.
The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.
| Главная Информация | |
|---|
| Добавка | - Антистатический
- Нуклеативный агент
|
| Характеристики | - Антистатический
- Блок сополимер
- Цикл быстрого формования
- Хороший поток
- Хороший выпуск пресс-формы
- Ядро
|
| Используется | - Колпачки
- Затворы
- Контейнеры
- Чашки
- Пищевая упаковка
- Упаковка
- Ведра
- Тонкостенная упаковка
|
| Номер файла UL | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238, ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 95 | | ASTM D785 |
| Твердость по суше (Shore D) | 62 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 1% Secant 1 | 1550 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1A/1 |
| Прочность на растяжение | | | |
| Yield 2 | 24.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2/1A/50 |
| Удлинение при растяжении | | | |
| Yield 3 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| -20°C | 5.0 | kJ/m² | |
| 0°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Зубчатый изод Impact | | | |
| -20°C | 45 | J/m | ASTM D256A |
| 0°C | 60 | J/m | ASTM D256A |
| 23°C | 70 | J/m | ASTM D256A |
| -20°C | 5.0 | kJ/m² | ISO 180/1A |
| 0°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Викат Температура размягчения | | | |
| -- | 150 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 76.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Примечание |
|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |