Описание материалов:
Vydyne R533 is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R533 resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-fiber reinforced PA66 resins over aluminum and/or zinc die-cast parts.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 33% наполнитель по весу
|
| Добавка | |
| Характеристики | - Хорошая химическая стойкость
- Хорошая коррозионная стойкость
- Хорошая стабильность размеров
- Хорошие электрические свойства
- Хороший поток
- Хороший выпуск пресс-формы
- Стабилизация тепла
- Высокая жесткость
- Высокая прочность
- Смазка
- Неагрессивных
|
| Используется | - Компоненты прибора
- Автомобильные Приложения
- Разъемы
- Электрическое/электронное применение
- Инженерные приложения
- Применение освещения
- Тонкостенные детали
|
| Рейтинг агентства | - Астм д 4066 PA0111G35
- Астм д 6779 PA0111G35
|
| Номер файла UL | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.40 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow
: 23°C, 2.00 mm | 0.40 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 0.80 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 10600 | 7900 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 205 | 145 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
| Флекторный модуль (23°C) | 10200 | 6500 | MPa | ISO 178 |
| Флекторный стресс (23°C) | 290 | 200 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | | ISO 527-2 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -30°C | 10 | 12 | kJ/m² | |
| 23°C | 11 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179 |
| -30°C | 70 | 85 | kJ/m² | |
| 23°C | 80 | 90 | kJ/m² | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -30°C | 10 | 12 | kJ/m² | |
| 23°C | 12 | 14 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 2.1E-5 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 100 | -- | °C | |
| 1.50 mm | 100 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.750 mm | 125 | -- | °C | |
| 1.50 mm | 125 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (3.00 mm) | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление (3.00 mm) | PLC 5 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 1 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 4 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 280 to 310 | °C | |
| Средняя температура | 280 to 310 | °C | |
| Передняя температура | 280 to 310 | °C | |
| Температура сопла | 280 to 310 | °C | |
| Температура обработки (расплава) | 285 to 305 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |