AGILITY™ 6047
| Категория | HDPE, Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | AGILITY™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
zVKqzG_AGILITY-6047.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
AGILITY 6047 is a Linear Medium Density Polyethylene, 1-Octene Copolymer from Dow. This resin offers good mechanical properties and toughness, with the required features for the production of diapers and products for feminine hygiene. This product is easy to process and has good web stability at high speed machines.
Main Characteristics:
Main Characteristics:
- Film for products for adult incontinence
- Film for diapers
- Film for products for feminine hygiene
- Easy to process and good web stability at high speed machines
- Complies with Regulation U.S. FDA 21 CFR 177.1520 (c) 3.2a
- Complies with Europe Commission Regulation (EU) No 10/2011
- Consult the regulations for complete details.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.947 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 20 | µm | |
| Сопротивление проколу пленки (20 µm) | 0.485 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| TD : 20 µm | 512 | MPa | ASTM D882 |
| 1% secant, TD : 20 µm | 428 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 327 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 20 µm | 15.1 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 15.1 | MPa | ASTM D882 |
| MD : Break, 20 µm | 12.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 10.3 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Yield, 20 µm | 9.7 | % | ASTM D882 |
| TD : Yield, 20 µm | 6.3 | % | ASTM D882 |
| MD : Break, 20 µm | 260 | % | ASTM D882 |
| TD : Break, 20 µm | 85 | % | ASTM D882 |
| Ударное падение Dart (20 µm) | 52 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 43 | g | ASTM D1922 |
| TD : 20 µm | 84 | g | ASTM D1922 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 235 | °C |
| Инструкции по экструзии |
|---|
| Recommended Processing Conditions for extrusion Cast for 20 um film: Die gap: 0,3 mm Line Speed: 19,7 m/min Melt Pressure: 81 bar Melt Temperature: 235°C Output: 7 kg/h Speed: 75 rpm |
| Тип материала | Категория | Производитель |
|---|---|---|
| MTEGRITY™ HDPE HD160 | HDPE | M. Holland Company |
| NEFTEKHIM PE 6948C (486H3) | HDPE | Nizhnekamskneftekhim Inc. |
| Braskem PE ES6004 | HDPE | Braskem |
| ETILINAS HD4202AA | HDPE | POLYETHYLENE MALAYSIA SDN BHD |
| Latistat 45/7-02 | HDPE | LATI S.p.A. |
| Petrothene® LT543501 | HDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved