Описание материалов:
Plexiglas® V920 is a General-purpose thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its very high melt flow. Plexiglas® V920 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V920 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.
| Главная Информация | |
|---|
| Характеристики | - Без BPA
- Хорошая стабильность цвета
- Хорошая стабильность размеров
- Хорошая термическая стабильность
- Хорошая устойчивость к ультрафиолетовому излучению
- Хорошая устойчивость к погоде
- Высокая четкость
- Высокая устойчивость к царапинам
- Низкая усадка
|
| Используется | - Автомобильные Приложения
- Потребительские приложения
- Оптическое применение
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1010
|
| Соответствие RoHS | |
| Внешний вид | - Прозрачный/прозрачный
- Доступные цвета
- Непрозрачный
- Полупрозрачный
|
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.18 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/3.8 kg) | 8.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.20 to 0.60 | % | ASTM D955 |
| Поглощение воды (24 hr) | 0.30 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (M-Scale) | 90 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3100 | MPa | ASTM D638 |
| Прочность на растяжение (Yield) | 68.9 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 5.0 | % | ASTM D638 |
| Флекторный модуль | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (23°C) | 16 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке 1 | | | ASTM D648 |
| 0.45 MPa, Annealed | 92.8 | °C | |
| 1.8 MPa, Annealed | 90.6 | °C | |
| Викат Температура размягчения | | | |
| -- | 100 | °C | ASTM D1525 2 |
| -- | 91.1 | °C | ASTM D1525 3 |
| Теплопроводность | 0.19 | W/m/K | ASTM C177 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | HB | | UL 94 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс преломления 4 | 1.490 | | ASTM D542 |
| Коэффициент пропускания (3180 µm) | 92.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 1.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| ASTM Classification | PMMA 0121V4 | | ASTM D788 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 79.4 to 87.8 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.10 | % | |
| Рекомендуемый размер снимка | 50 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 204 | °C | |
| Средняя температура | 210 | °C | |
| Передняя температура | 216 | °C | |
| Температура сопла | 210 | °C | |
| Температура обработки (расплава) | < 271 | °C | |
| Температура формы | 65.6 to 85.0 | °C | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Отношение винта L/D | 15.0:1.0 to 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.0:1.0 to 2.5:1.0 | | |
| Глубина вентиляционного отверстия | 0.051 | mm | |
| Примечание |
|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |