LUVOCOM® 1105-0904/GN

Категория PEEK, Polyetheretherketone
Производитель LEHVOSS Group
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF z4VLkF_LUVOCOM11050904GN.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1105-0904/GN is a polyetheretherketone (PEEK) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main characteristics of 1105-0904/GN are:
  • flame retardant/rated flame
  • Flame Retardant
  • sterilizable
  • Good dimensional stability
  • Good stiffness

Typical application areas include:
  • textile/fiber
  • engineering/industrial accessories
  • Aerospace
  • Automotive Industry
  • medical/health care
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал
Характеристики
  • Хорошая стабильность размеров
  • Жесткий, хороший
  • Хорошая прочность
  • Хорошая химическая стойкость
  • Теплостойкость, высокая
  • Сопротивление гидролизу
  • Биологическая Совместимость
  • Паровая дезинфекция
  • Огнестойкий
Используется
  • Текстильные изделия
  • Инженерные аксессуары
  • Аэрокосмическое применение
  • Применение в автомобильной области
  • Медицинские принадлежности/принадлежности для ухода
Внешний вид
  • Зеленый
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.55g/cm³ISO 1183
Формовочная усадка 0.30 - 0.70%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.10%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 11000MPaISO 527-2
Tensile Stress (Break)150MPaISO 527-2
Растяжимое напряжение (Yield)2.0%ISO 527-2
Флекторный модуль 9000MPaISO 178
Флекторный стресс 210MPaISO 178
Flexural Strain at Flexural Strength 2.5%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 280°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance > 1.0E+12ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)35kJ/m²ISO 179/1fU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 250°CUL 746B
Викат Температура размягчения 325°CISO 306/A
CLTE- Поток 2.2E-5cm/cm/°CDIN 53752
Теплопроводность 0.40W/m/KDIN 52612
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость 1V-0UL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    Hot air dryer, A 150°C
    Hot air dryer, B 120°C
Время сушки
    Hot air dryer, A 3.0 - 6.0hr
    Hot air dryer, B 6.0 - 8.0hr
Задняя температура 360 - 370°C
Средняя температура 380 - 390°C
Передняя температура 390 - 400°C
Температура сопла 360 - 380°C
Температура обработки (расплава) 390°C
Температура формы 170 - 200°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Примечание
1 .Not recognized by UL.
Тип материала Категория Производитель
SCHULATEC® PEEK CF 30 NV 12 PEEK A. Schulman Europe
Arlon® 1260 PEEK Greene, Tweed & Co.
LUVOCOM® 1105-7194/GY PEEK LEHVOSS Group
RTP 2282 PEEK RTP Company
RTP 2283 HF TFE 15 PEEK RTP Company
LUVOCOM® 1105-7714 PEEK Lehmann & Voss & Co.
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами