Braskem PE PLURIS4301
| Категория | LLDPE, Linear Low Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
z0SZ97_Braskem-PE-PLURIS4301.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Pluris4301 is a Braskem Quaterpolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content.
Applications:
Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others.
Additive:
Process:
Blown Film Extrusion
Applications:
Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others.
Additive:
- Antiblocking medium
- Slip medium
Process:
Blown Film Extrusion
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.922 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение | ASTM D882 | ||
| MD : Fracture, 38 µm | 32.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 33.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 38 µm | 920 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1500 | % | ASTM D882 |
| Флекторный модуль | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 310 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 400 | MPa | ASTM D790 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 50 | g | ASTM D1922 |
| TD : 38 µm | 300 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60°, 38.0 µm) | 45 | ASTM D2457 | |
| Haze | 43 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Recommended Blown Film Extrusion Conditions: Temperature Profile: 150°C to 170°C Blow Up Ratio: 2 to 3:1 Die Gap: 1.8 to 2.5 mm Mass Temperature: 160° to 200°C It's Recommended to add 20 to 30% LDPE to be obtained excellent optical propert |
| Тип материала | Категория | Производитель |
|---|---|---|
| SAPYLENE MC75LTD | LLDPE | Sahel Chimie Co. |
| SEETEC LLDPE UF917 | LLDPE | Lotte Chemical Corporation |
| Sumitomo PE FS150A | LLDPE | Sumitomo Chemical Asia |
| Titanvene™ LL0220SR | LLDPE | PT. TITAN Petrokimia Nusantara |
| TOTAL Polyethylene Lumicene® M 2711 PCE | LLDPE | TOTAL Refining & Chemicals |
| Clearflex® H&T FGH 196 | LLDPE | Versalis S.p.A. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved