Описание материалов:
Ultramid 8253 is an unreinforced, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/or pigmented versions. Copolymerization results in improved dry as molded toughness and increased flexibility to meet higher impact performance compared to conventional unreinforced homopolymers. Good nylon thermal and chemical properties are maintained along with good strength and stiffness retention.
Applications
Ultramid 8253 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips, fasteners, flanges, key housings as well as many flexible tubing applications.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Сополимер
- Хорошая химическая стойкость
- Хорошая гибкость
- Хорошая ударопрочность
- Хорошая жесткость
- Хорошая прочность
- Хорошая прочность
- Модификация удара
|
| Используется | - Электрические детали
- Крепежные детали
- Корпуса
- Оборудование для газонов и сада
- Вилки
- Защитные покрытия
- Трубка
|
| Рейтинг агентства | |
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Многоточечные данные | - Модуль сдвига против температуры (ISO 11403-1)
- Вязкость по сравнению со скоростью сдвига (ISO 11403-2)
|
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.09 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Формовочная усадка-
Поток (3.18 mm) | 1.2 | -- | % | |
| Поглощение воды | | | | |
| 24 hr | 1.5 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.5 | -- | % | ISO 62 |
| Saturation | 8.1 | -- | % | ASTM D570 |
| Saturation, 23°C | 8.1 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.3 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Твердость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 82 | -- | | ASTM D785 |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | | ISO 527-2 |
| -40°C | 2840 | 3300 | MPa | |
| 23°C | 2300 | 730 | MPa | |
| 80°C | 400 | 370 | MPa | |
| 121°C | 295 | 220 | MPa | |
| Прочность на растяжение | | | | |
| Yield, -40°C | 117 | 116 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 65.0 | 32.0 | MPa | ASTM D638 |
| Yield, 80°C | 25.0 | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 20.0 | -- | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 60.0 | 32.0 | MPa | ISO 527-2 |
| Break, -40°C | 100 | 70.0 | MPa | ASTM D638 |
| Break, 23°C | 60.0 | -- | MPa | ASTM D638 |
| Удлинение при растяжении | | | | |
| Yield, -40°C | 7.0 | -- | % | ASTM D638 |
| Yield, 23°C | 4.0 | 15 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 29 | -- | % | ASTM D638 |
| Yield, 121°C | 34 | 30 | % | ASTM D638 |
| Break, -40°C | 9.0 | 20 | % | ASTM D638 |
| Break, 23°C | > 100 | > 100 | % | ASTM D638 |
| Номинальное растяжение при разрыве (23°C) | 40 | > 50 | % | ISO 527-2 |
| Флекторный модуль | | | | |
| -40°C | 3050 | 3150 | MPa | ASTM D790 |
| 23°C | 2210 | 670 | MPa | ASTM D790 |
| 65°C | 415 | -- | MPa | ASTM D790 |
| 90°C | 325 | -- | MPa | ASTM D790 |
| 121°C | 260 | -- | MPa | ASTM D790 |
| 23°C | 1900 | -- | MPa | ISO 178 |
| Flexural Strength | | | | |
| -40°C | 148 | 141 | MPa | ASTM D790 |
| 23°C | 87.0 | 32.0 | MPa | ASTM D790 |
| 65°C | 25.0 | -- | MPa | ASTM D790 |
| 90°C | 20.0 | -- | MPa | ASTM D790 |
| 121°C | 14.0 | -- | MPa | ASTM D790 |
| 23°C | 65.0 | -- | MPa | ISO 178 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 18 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | | ISO 179 |
| Зубчатый изод Impact | | | | ASTM D256 |
| -40°C | 80 | 64 | J/m | |
| 23°C | 150 J/m | No Break | | |
| Drop Impact Resistance (23°C) | 271 | -- | J | Internal Method |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | | |
| 0.45 MPa, Unannealed | 168 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| Пиковая температура плавления | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE | | | | |
| Flow | 9.9E-5 | -- | cm/cm/°C | ASTM E831 |
| Flow | 8.8E-5 | -- | cm/cm/°C | |
| Transverse | 9.3E-5 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.710 mm | 105 | -- | °C | |
| 0.750 mm | 105 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| 6.00 mm | 75.0 | -- | °C | |
| RTI Str | | | | UL 746 |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C | |
| 6.00 mm | 85.0 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | | | | |
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| 6.00 mm | HB | -- | | |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Рекомендуемая максимальная влажность | 0.20 | % | |
| Температура обработки (расплава) | 240 to 270 | °C | |
| Температура формы | 60.0 to 85.0 | °C | |
| Давление впрыска | 3.50 to 12.5 | MPa | |
| Скорость впрыска | Fast | | |