SABIC® LDPE HP2022J
| Категория | LDPE, Low Density Polyethylene |
| Производитель | SABIC Americas, Inc. |
| Торговая марка | SABIC® LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
yGEbAn_SABIC-LDPE-HP2022J.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Product Description
HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good opticals and mechanical properties.
Typical Applications
Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general purpose bags with good optics and t-shirts carrier bags.
HP2022J: 750 ppm Slip & 1000 ppm Antiblock
HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good opticals and mechanical properties.
Typical Applications
Thin shrink film, lamination film, produce bags, textile packaging, soft goods packaging, general purpose bags with good optics and t-shirts carrier bags.
HP2022J: 750 ppm Slip & 1000 ppm Antiblock
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.922 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/21.6 kg) | 0.75 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 30 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD : 30 µm, blown film | 160 | MPa | ASTM D882 |
| 1% secant, TD : 30 µm, blown film | 180 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 30 µm, blown film | 8.00 | MPa | ASTM D882 |
| TD : Yield, 30 µm, blown film | 7.00 | MPa | ASTM D882 |
| MD : Broken, 30 µm, blown film | 21.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 18.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 290 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 570 | % | ASTM D882 |
| Ударное падение Dart (30 µm, Blown Film) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, blown film | 180 | g | ASTM D1922 |
| TD : 30 µm, blown film | 150 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 92.0 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 30.0 µm, Blown Film) | 80 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | ||
|---|---|---|---|
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured by producing 30 µ film with 2.5 BUR using 100% HP2022N. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 160 - 180 | °C |
| Тип материала | Категория | Производитель |
|---|---|---|
| Trithene® TS 7028 | LDPE | Petroquimica Triunfo |
| DOW™ LDPE 535E | LDPE | The Dow Chemical Company |
| CERTENE™ LDF-0824B | LDPE | Muehlstein |
| GETILAN MAC/900 | LDPE | Crosspolimeri S.p.A. |
| Cheng Yu BK1020 | LDPE | Cheng Yu Plastic Company Limited |
| Osterlene® LD-3-931 | LDPE | Osterman & Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved