DOW™ LDPE 535E
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
y3gkrm_DOW-LDPE-535E.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOW LDPE 535E is a medium density LDPE with a melt index of 0.6. It is suitable for the processing of shrink films and has a good balance between shrinkage properties (heat shrinkage and cold shrinkage), optical properties such as high gloss and low haze, and mechanical properties.
Main features:
EU, No 10/2011
please consult the regulation for complete details.
Main features:
- Low density polyethylene resin
- Extrusion of blown film
- heat shrinkable film
- Comply with the following regulations:
EU, No 10/2011
please consult the regulation for complete details.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.928 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения | 0.30 - 0.45 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 211 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 219 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 13.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 370 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 530 | % | ASTM D882 |
| Ударное падение Dart (50 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 230 | g | ASTM D1922 |
| TD : 50 µm, blown film | 230 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 104 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.0 µm) | 62 | ASTM D2457 | |
| Haze (50.0 µm) | 8.3 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 放大比：1 比 2.5 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sinpolene MBB3462 | LDPE | Teknor Apex Asia Pacific PTE. LTD. |
| MTEGRITY™ LDPE LD220MM | LDPE | M. Holland Company |
| DOW™ LDPE 748I | LDPE | The Dow Chemical Company |
| CERTENE™ LDF-120J | LDPE | Muehlstein |
| Kemcor LD 0231 | LDPE | Qenos Pty Ltd |
| INEOS LDPE 28H430 | LDPE | INEOS Olefins & Polymers Europe |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved