Описание материалов:
Hyflon® F is a unique new family of MFA polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low surface energy and exceptional dielectric properties.
Hyflon® MFA F1520 is a low melt flow rate multi purpose resin with an exceptional stress crack resistance, continuous service temperature up to 225°C and a 100-150x10³ cycles flex-life (on a 0.3mm flim, ASTM D2176).
| Главная Информация | |
|---|
| Характеристики | - Высокий уровень ЭСКП (устойчивость к растрескиванию)
- Хорошая гибкость
- Низкий уровень жидкости
- Огнестойкий
|
| Используется | - Применение проводов и кабелей
- Универсальный
|
| Соответствие RoHS | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 2.10 - 2.15 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (372°C/5.0 kg) | 1.0 - 4.0 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 55 - 60 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1(23°C) | 400 - 500 | MPa | ASTM D3307 |
| Прочность на растяжение 2(Break, 23°C) | > 30.0 | MPa | ASTM D3307 |
| Удлинение при растяжении 3(Break, 23°C) | > 300 | % | ASTM D3307 |
| Срок службы изгиба 4 | 1.0E+5 - 1.5E+5 | Cycles | ASTM D2176 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Тепло кристаллизации | 16.0 - 24.0 | J/g | DSC |
| Тепло плавления | 16.0 - 24.0 | J/g | DSC |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура фланца | 370 - 400 | °C | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура плавления | 265 - 275 | °C | ASTM D3307 |
| Пиковая температура кристаллизации (DSC) | 255 - 265 | °C | DSC |
| CLTE-
Поток | 1.2E-4 - 2.0E-4 | cm/cm/°C | ASTM D696 |
| Удельный нагрев (23°C) | 900 - 1100 | J/kg/°C | DSC |
| Теплопроводность (40°C) | 0.20 | W/m/K | ASTM C177 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | > 1.0E+17 | ohms | ASTM D257 |
| Сопротивление громкости | > 1.0E+17 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность 5(1.00 mm) | 35 - 40 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная | | | ASTM D150 |
| 23°C, 50 Hz | 2.00 | | ASTM D150 |
| 23°C, 100 kHz | 2.00 | | ASTM D150 |
| Коэффициент рассеивания | | | ASTM D150 |
| 23°C, 50 Hz | < 5.0E-4 | | ASTM D150 |
| 23°C, 100 kHz | < 5.0E-4 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Индекс кислорода | 95 | % | ASTM D2863 |
| Дополнительная информация |
|---|
| COLOR MASTER BATCHES
We recommend that only Color Master Batches based in Hyflon MFA be used. Master Batches based on other fluoropolymers can negatively influence the superior processing and electrical performance of the resin. A list of suppliers can be obtained from your Solvay sales representative.
HEALTH SAFETY AND ENVIRONMENT
Hyflon MFA F1520 is a very inert polymer and it is not harmful if used and handled according to standard processing procedures. If handled inappropriately, it may release harmful toxic chemicals.
Hyflon MFA F1520 does not contain any RoHS or WEEE substances. Hyflon MFA F1520 is not produced using APFO and contains no APFO. Please refer to the Material Safety Data Sheets for more information on handling and safety.
PACKAGING AND STORAGE
Hyflon MFA F1520 resin is available in 25 kg (55 lbs) and 500 kg (1102 lbs) packaging. Though it has an indefinite shelf life, it is recommended to store it in a clean area, protected by direct sun light and possible contamination. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 240 - 290 | °C | |
| Зона цилиндра 2 температура. | 270 - 320 | °C | |
| Зона цилиндра 3 темп. | 300 - 360 | °C | |
| Зона цилиндра 4 темп. | 320 - 380 | °C | |
| Зона цилиндра 5 темп. | 340 - 390 | °C | |
| Температура адаптера | 370 - 400 | °C | |
| Температура расплава | 400 | °C | |
| Температура матрицы | 390 - 420 | °C | |
| Инструкции по экструзии |
|---|
| EXTRUSION PROCESSING GUIDELINES
As with other fluoropolymers, Hyflon MFA is corrosive in the melt. Therefore all parts coming into prolonged contact with the melt should be made with corrosion resistant materials such as Hastelloy®, Inconel®, Monel® or Xaloy®. Chrome or nickel plating is not recommended since they are typically only sufficient for brief processing tests.
F1520 is suitable for extrusion using techniques normally applied for other thermo-processable plastics, provided that the extruder is equipped with corrosion resistant alloys. Extruders with L/D ratio of 20:1 to 30:1 are recommended. Extruders should be equipped with independently controlled heaters capable of accurate temperature control up to 450°C (840°F). An overview of the temperature, tooling and equipment requirements are in the following tables.
Many different screw designs can be used. Single-flight screws are recommended while barrier-flights should be avoided. A typical screw design consist of a long feed section (at least 12 flights), followed by a 2 to 6 flight transition and a 5 to 7 flight metering section. |
| Примечание |
|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 0.3mm film |
| 5 . | 50Hz |