LUVOCOM® 3-7901

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	x5g96n_LUVOCOM-3-7901.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®3-7901 is a polyamide 6 (nylon 6) material, which contains glass and carbon fiber reinforced materials. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 3-7901 are:

Conductivity

Electrostatic protection

Good stiffness

Wear-resistant

Typical application areas include:

engineering/industrial accessories

House

textile/fiber

Automotive Industry

Handle

Главная Информация
Наполнитель/армирование	Армированные материалы из стекла и углеродного волокна
Характеристики	Проводящий Жесткий, хороший Защита от электростатического разряда Хорошая прочность Хорошая стойкость к истиранию
Используется	Ручка Текстильные изделия Инженерные аксессуары Ролик Применение в автомобильной области Чехол
Внешний вид	Синий

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.44	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.50	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 1.0	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	14000	MPa	ISO 527-2
Tensile Stress (Break)	165	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.2	%	ISO 527-2
Флекторный модуль	24000	MPa	ISO 178
Флекторный стресс	230	MPa	ISO 178
Flexural Strain at Flexural Strength	2.5	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	130	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0E+4	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	43	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	110	°C	UL 746B

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	75.0	°C
B	105	°C
Время сушки
A	10 - 16	hr
B	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.10	%
Задняя температура	250 - 270	°C
Средняя температура	270 - 290	°C
Передняя температура	280 - 300	°C
Температура сопла	270 - 280	°C
Температура обработки (расплава)	270	°C
Температура формы	70.0 - 110	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
TEREZ PA 6 7850 T GK 30	Nylon 6	TER HELL PLASTIC GMBH
Next Nylon 6 Prime Series NGIM30-01BK	Nylon 6	Next Polymers Ltd.
Electrafil® PA6 GF20 AS BK	Nylon 6	Techmer Engineered Solutions
Grilon® F 47 H NL nat 6020	Nylon 6	EMS-GRIVORY
DINALON® PA 6 30% CM	Nylon 6	Grupo Repol
Durethan® BKV 50 H2.0 EF 900116	Nylon 6	LANXESS GmbH