Viton® A-361C

Категория	FKM, Fluoroelastomer , Fluorelastomer
Производитель	DuPont Performance Elastomers
Торговая марка	Viton®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	w7Z8GF_Viton-A-361C.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Viton A-361C is an incorporated cure A-family dipolymer designed for the injection and transfer molding of parts requiring better metal adhesion along with the fluid and heat resistance characteristics typical of fluoroelastomers. The moderate viscosity level of Viton A-361C also allows for satisfactory compression molding of parts. Features of Viton A-361C are:
-Intermediate viscosity level (when compared with Viton A-201C/Viton A-401C)
-Fully precompounded
--reduced curative level
--incorporated metal adhesion promoter
-Improved processing
--increased mold flow
--easier mold release with less mold fouling
--improved demolding "hot tear"
-Good metal bonding with standard industrial primers

Applications:
Compression, transfer, and injection molding of:
-O-rings and gaskets
-Valve stem and crankshaft seals (and other bonded parts requiring fluid and heat resistance of the A-family of Viton)

Главная Информация
Добавка	УГЛЕРОДНЫЙ черный (30)
Характеристики	Хорошая мобильность
Используется	Труба Фитинги для труб Уплотнение Нанесение покрытия
Внешний вид	Белый
Формы	Лист
Метод обработки	Экструзия Литье из смолы Прессформа сжатия Каландрирование Литье под давлением

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	1.81	g/cm³	ASTM D792
Вязкость Mooney (ML 1+10, 121°C)	63	MU	ASTM D1646

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore A)	78		ASTM D2240

Эластомеры	Номинальное значение	Единица измерения	Метод испытания
Tensile Stress (100% Strain)	3.80	MPa	ASTM D412
Прочность на растяжение (Break)	9.50	MPa	ASTM D412
Удлинение при растяжении (Break)	300	%	ASTM D412
Комплект сжатия
23°C, 70 hr	7.0	%	ASTM D395B
200°C, 70 hr	17	%	ASTM D395
232°C, 70 hr	37	%	ASTM D395B

Старение	Номинальное значение	Единица измерения	Метод испытания
Изменение прочности на растяжение в воздухе			ASTM D573
200°C, 70 hr	24	%	ASTM D573
100% strain, 200°C, 70 hr	24	%	ASTM D573
200°C, 168 hr	26	%	ASTM D573
100% strain, 200°C, 168 hr	32	%	ASTM D573
232°C, 24 hr	34	%	ASTM D573
100% strain, 232°C, 24 hr	31	%	ASTM D573
232°C, 70 hr	27	%	ASTM D573
100% strain, 232°C, 70 hr	27	%	ASTM D573
Изменение максимального удлинения в воздухе			ASTM D573
200°C, 70 hr	-43	%	ASTM D573
200°C, 168 hr	-45	%	ASTM D573
232°C, 24 hr	-39	%	ASTM D573
232°C, 70 hr	-43	%	ASTM D573
Изменение твердости дюрометра в воздухе			ASTM D573
Support a, 200°C, 70 hr	-2.0		ASTM D573
Support a, 200°C, 168 hr	1.0		ASTM D573
Support a, 232°C, 24 hr	-1.0		ASTM D573
Support a, 232°C, 70 hr	-2.0		ASTM D573

Дополнительная информация
Mooney Scorch, MS at 121°C, Minimum: 33 in-lbMooney Scorch, MS at 121°C, 5 unit rise: >30 minODR at 177°C, Microdie, 3° Arc, 15 min:ML: 14 in-lbts2: 1.9 mintc90: 3.7 minMc90: 92 in-lbMH: 100 in-lbRosand Capillary Rheometer at 100°C, 1.5 mm Die, L/D=0/112.7 mm/min, 113 s^-1: 6.8 MPa50.8 mm/min, 452 s^-1: 10.2 MPa127 mm/min, 1130 s^-1: 16.1 MPaNominal Viscosity, ML 1 + 10, 121°C: 30Polymer Fluorine Content: 66%

Дополнительная информация

Mooney Scorch, MS at 121°C, Minimum: 33 in-lbMooney Scorch, MS at 121°C, 5 unit rise: >30 minODR at 177°C, Microdie, 3° Arc, 15 min:ML: 14 in-lbts2: 1.9 mintc90: 3.7 minMc90: 92 in-lbMH: 100 in-lbRosand Capillary Rheometer at 100°C, 1.5 mm Die, L/D=0/112.7 mm/min, 113 s^-1: 6.8 MPa50.8 mm/min, 452 s^-1: 10.2 MPa127 mm/min, 1130 s^-1: 16.1 MPaNominal Viscosity, ML 1 + 10, 121°C: 30Polymer Fluorine Content: 66%

Тип материала	Категория	Производитель
Viton® B-601C	Fluorelastomer	DuPont Performance Elastomers
Boda BDF-LG2701	Fluorelastomer	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Boda BDF-KR2701	Fluorelastomer	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Boda BDT-LB3752	Fluorelastomer	Chenguang Fluoro & Silicone Elastomers Co., Ltd.
Cri-Line SP-715	Fluorelastomer	Cri-Tech, Inc.
3M™ Dyneon™ Fluoroelastomer FE 5620Q	Fluorelastomer	3M Advanced Materials Division