Cariflex® IR0310 K
| Категория | IR, Polyisoprene |
| Производитель | Kraton Polymers LLC |
| Торговая марка | Cariflex® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
ufb5XG_Cariflex-IR0310-K.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Cariflex IR0310 KU polymer is a solution polymerised polyisoprene with a high cis-1,4 content. It has a high molecular weight as indicated by its Logarithmic Inherent Viscosity (LIV) value of 7.05 dl/g. It is supplied from North America in the physical form identified below.
A non-staining stabilizer is added at the typical value of 0.15%. Cariflex IR0310 KU polymer is manufactured to the highest standards but special requirements apply to certain sensitive applications such as food contact and pharmaceuticals. Reference should always be made to local legislation regulating these applications.
Cariflex IR0310 KU Polymer is used as a replacement for natural rubber in a wide range of compounds, offering advantages of light color, uniformity and low levels of impurities. Its good flow characteristics produce improvements in mixing and molding behavior. It is used for food and pharmaceutical packaging and seals, baby bottle teats and health care, adhesives, chemical derivatives of rubbers and very light colored or transparent articles.
- Cariflex IR0310 KU - supplied as a white/transparent solid bale
A non-staining stabilizer is added at the typical value of 0.15%. Cariflex IR0310 KU polymer is manufactured to the highest standards but special requirements apply to certain sensitive applications such as food contact and pharmaceuticals. Reference should always be made to local legislation regulating these applications.
Cariflex IR0310 KU Polymer is used as a replacement for natural rubber in a wide range of compounds, offering advantages of light color, uniformity and low levels of impurities. Its good flow characteristics produce improvements in mixing and molding behavior. It is used for food and pharmaceutical packaging and seals, baby bottle teats and health care, adhesives, chemical derivatives of rubbers and very light colored or transparent articles.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Вязкость Mooney | 40 to 53 | MU | ASTM D1646 |
| 1,4-cis содержание | Internal Method | ||
| -- 1 | > 82.0 | wt% | |
| -- 2 | > 90.0 | wt% | |
| Содержание золы | < 0.10 | % | Internal Method |
| Limiting Viscosity Number | 700 to 1050 | cm³/g | Internal Method |
| Стабилизатор | 0.10 to 0.30 | % | Internal Method |
| Летучее вещество | < 0.50 | % | Internal Method |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress 3(300% Strain) | 7.30 to 12.2 | MPa | ISO 37 |
| Растяжимое напряжение- Поток 4(Yield) | > 21.6 | MPa | ISO 37 |
| Удлинение при растяжении 5(Break) | > 430 | % | ISO 37 |
| Примечание | |
|---|---|
| 1 . | NMR |
| 2 . | FTIR |
| 3 . | Cure: 40 min at 135°C |
| 4 . | Cure: 40 min at 135°C |
| 5 . | Cure: 40 min at 135°C |
| Тип материала | Категория | Производитель |
|---|---|---|
| Nipol® IR2200L | IR | Zeon Chemicals L.P. |
| Nipol® IR 2200 | IR | Zeon Corporation |
| Nipol® IR 2200L | IR | Zeon Corporation |
| SIBUR Synthetic Rubber IR SKI-3 Group I | IR | SIBUR |
| SIBUR Synthetic Rubber IR SKI-3 NST Group II | IR | SIBUR |
| Cariflex® IR0310 K | IR | Kraton Polymers LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved