Описание материалов:
Monprene MP-2104 is a general purpose thermoplastic elastomer designed for a variety of consumer product applications requiring a soft, rubber-like feel. Monprene MP-2104 is a low hardness, opaque grade that exhibits excellent mold release, suitable for injection molding and extrusion.
| Главная Информация | |
|---|
| Характеристики | - Высокая эластичность
- Хорошая мобильность
- Хорошая гибкость
- Хорошая прочность на разрыв
- Хорошая окраска
- Хорошая производительность при потере
|
| Используется | - Оборудование для безопасности
- Ручка
- Мягкая ручка
- Спортивные товары
- Канцелярские принадлежности
- Применение потребительских товаров
- Ручка зубной щетки
|
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.878 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/2.16 kg | 1.5 | g/10 min | ASTM D1238 |
| 200°C/5.0 kg | 18 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 30 | | ASTM D2240 |
| Shaw A, 5 seconds | 28 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 0.689 | MPa | ASTM D412 |
| 300% strain | 1.34 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 6.48 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 820 | % | ASTM D412 |
| Прочность на разрыв-
Поток 1 | 22.6 | kN/m | ASTM D624 |
| Комплект сжатия (23°C, 22 hr) | 12 | % | ASTM D395 |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Задняя температура | 182 - 232 | °C | |
| Средняя температура | 188 - 238 | °C | |
| Передняя температура | 193 - 243 | °C | |
| Температура сопла | 199 - 249 | °C | |
| Температура обработки (расплава) | 199 - 249 | °C | |
| Температура формы | 16 - 32 | °C | |
| Давление впрыска | 1.38 - 5.52 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Подушка | 3.81 - 25.4 | mm | |
| Инструкции по впрыску |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 182 - 232 | °C | |
| Зона цилиндра 2 температура. | 188 - 238 | °C | |
| Зона цилиндра 3 темп. | 193 - 243 | °C | |
| Зона цилиндра 4 темп. | 193 - 243 | °C | |
| Зона цилиндра 5 темп. | 199 - 249 | °C | |
| Температура матрицы | 199 - 249 | °C | |
| Инструкции по экструзии |
|---|
| 螺杆转速30 - 100 rpm |