LUVOCOM® 1850-7581

Категория PBT, Polybutylene Terephthalate
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF udQ6rg_LUVOCOM-1850-7581.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1850-7581 is a polybutene terephthalate (PBT) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1850-7581 are:
  • Conductivity
  • Electrostatic protection
  • Lubrication

Typical application areas include:
  • Electrical/electronic applications
  • Reflector
  • textile/fiber
  • engineering/industrial accessories
  • Automotive Industry
Главная Информация
Наполнитель/армирование
  • Армированный материал из углеродного волокна
Добавка
  • Ptfe лубрикант
Характеристики
  • Проводящий
  • Защита от электростатического разряда
  • Смазка
Используется
  • Электрическое/электронное применение
  • Зеркало
  • Текстильные изделия
  • Инженерные аксессуары
  • Переключатель
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Катушка
Внешний вид
  • Черный
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.52g/cm³ISO 1183
Плавкий объем-расход (MVR) (250°C/5.0 kg)11.0cm³/10minISO 1133
Формовочная усадка 0.10 - 0.40%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.10%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 20000MPaISO 527-2
Tensile Stress (Break)140MPaISO 527-2
Растяжимое напряжение (Yield)1.3%ISO 527-2
Флекторный модуль 17000MPaISO 178
Флекторный стресс 195MPaISO 178
Коэффициент трения
    Dynamic 0.14
    Static 0.10
Flexural Strain at Flexural Strength 1.6%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 180°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)30kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)210°CISO 75-2/A
Температура непрерывного использования 130°CUL 746B
Викат Температура размягчения 210°CISO 306/A
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 120°C
    Vacuum dryer, B 80.0°C
Время сушки
    A 4.0 - 6.0hr
    Vacuum dryer, B 6.0 - 8.0hr
Рекомендуемая максимальная влажность 0.020%
Задняя температура 240 - 260°C
Средняя температура 260 - 280°C
Передняя температура 250 - 270°C
Температура сопла 250 - 265°C
Температура обработки (расплава) 250°C
Температура формы 60.0 - 120°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Тип материала Категория Производитель
RTP 1000 TFE 20 SI 5 PBT RTP Company
HONES® PBT GT20 PBT Guangdong Shunde Hones Polymer Material Co., Ltd.
RAMSTER PF340S6 PBT Polyram Ram-On Industries
SLOVASTER® B1 GF 6 PBT Plastcom
VESTODUR® GF50 PBT Evonik Industries AG
Ultradur® B 4040 G10 BK5110 PBT BASF Corporation
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами