Описание материалов:
HTA 002 is a general medium molecular weight grade, which is characterized by easy processability, especially in coextrusion and mixing with other polyolefins. HTA 002 can also be used alone, which is especially suitable for easy processing and conversion into small and thin bags for light weight packaging.
| Главная Информация | |
|---|
| Добавка | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/21.6 kg | 16 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.68 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD | 960 | MPa | ASTM D882 |
| 1% secant, TD | 1200 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield | 29.0 | MPa | ASTM D882 |
| TD
: Yield | 29.0 | MPa | ASTM D882 |
| MD
: Fracture | 55.0 | MPa | ASTM D882 |
| TD
: Fracture | 50.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Fracture | 320 | % | ASTM D882 |
| TD
: Fracture | 450 | % | ASTM D882 |
| Ударное падение Dart | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD | 8.0 | g | ASTM D1922 |
| TD | 60 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 126 | °C | ASTM D1525 |
| Юридическое заявление |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |