Описание материалов:
Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 96 | | ASTM D2240 |
| Shaw D | 43 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 1.17 | MPa | ASTM D695 |
| 5% strain | 2.41 | MPa | ASTM D695 |
| 10% strain | 3.79 | MPa | ASTM D695 |
| 15% strain | 5.17 | MPa | ASTM D695 |
| 20% strain | 6.76 | MPa | ASTM D695 |
| 25% strain | 8.27 | MPa | ASTM D695 |
| Устойчивость к истиранию | 16.9 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 10.0 | MPa | ASTM D412 |
| 300% strain | 17.2 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 31.0 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 550 | % | ASTM D412 |
| Комплект сжатия | 35 | % | ASTM D395 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 10 | min | |
| Время демолд | 90 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 765 pliAverage Split Tear, ASTM D1938: 425 pliStoichiometry Curative Level: 90%Break Set, ASTM D412-80: 40%NBS Abrasion: 385% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 13.93 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 14.04 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 14.14 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 14.25 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 14.36 parts by weightMix Temperature:
Andur M-22: 221-230°F
Curative HQEE: 230°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 110 - 140 | °C | |