Escor™ 5100

Категория	EAA, Ethylene Acrylic Acid Copolymer Resin
Производитель	ExxonMobil Chemical
Торговая марка	Escor™
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	tClvvT_Escor-5100.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Escor 5100 is mainly used for extrusion coating, coextrusion coating and extrusion compounding. It can be well bonded to polar substrates, aluminum foils, metal films, paper, steel and glass surfaces. It also has high binding resistance when used in packaging acidic food. Excellent coextruded adhesive resin for polyamide. Excellent heat sealing performance: extremely low temperature heat sealing and high heat sealing strength, high thermal adhesion and good anti-pollution heat sealing. Excellent adhesive polymer in film.

Главная Информация

Физический	Номинальное значение	Единица измерения	Метод испытания
Массовый расход расплава (MFR) (190°C/2.16 kg)	8.5	g/10 min	ASTM D1238
Содержание акриловой кислоты	11.0	wt%	ExxonMobil Method

Юридическое заявление
有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用

Инструкции по экструзии
Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Инструкции по экструзии

Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Тип материала	Категория	Производитель
Escor™ 5200	EAA	ExxonMobil Chemical
BONDINE® HX8210	EAA	Arkema
Bynel® 2002	EAA	DuPont Packaging & Industrial Polymers
Lotader® HX8290	EAA	Arkema
PRIMACOR™ 1410	EAA	The Dow Chemical Company
Bynel® 2022	EAA	DuPont Packaging & Industrial Polymers