OnForce™ LFT LF5200-5003 NATURAL
Описание материалов:
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.
| Главная Информация | |
|---|
| Наполнитель/армирование | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.28 | g/cm³ | ISO 1183 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break) | 1.7 | % | ISO 527-2 |
| Флекторный модуль | 8900 | MPa | ISO 178 |
| Флекторный стресс | 190 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | 26 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 78 | kJ/m² | ISO 179 |
| Ударное падение Dart | 123 | J | ASTM D5420 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 2.0 | hr | |
| Температура обработки (расплава) | 210 - 230 | °C | |
| Температура формы | 60.0 | °C | |
| Скорость впрыска | Slow-Moderate | | |
| Back Pressure | 1.00 | MPa | |
| Инструкции по впрыску |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed. |