Описание материалов:
Production-Grade Thermoplastic for Fortus 3D Production Systems

PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resistance of PC and the flexibility of ABS. PC-ABS blends are commonly used in automotive, electronics and telecommunications applications. Additionally, a PC-ABS part manufactured on a Fortus® 3D Production System is 5-60 percent stronger than a part made on previous FDM® systems. When combined with a Fortus system, PC-ABS gives you Real Parts™ conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts.
Главная Информация
Характеристики
  • Прочный
  • Хорошая химическая стойкость
  • Хорошая гибкость
  • Хорошая стерилизация
  • Хорошая прочность
  • Высокая термостойкость
  • Высокая ударопрочность
Используется
  • Автомобильные Приложения
  • Электрическое/электронное применение
  • Инженерные детали
  • Промышленное применение
  • Прототипирование
  • Телекоммуникации
  • Оснастка
Номер файла UL
  • E345258
Внешний вид
  • Черный
Метод обработки
  • 3D печать, Плавленая нить (FFF)
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес 1.10g/cm³ASTM D792
Толщина- Возможность слоя 127.0 to 330.2µm
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Сопротивление громкости 14.4E+13 to 2.0E+14ohmsASTM D257
ТвердостьНоминальное значениеЕдиница измеренияМетод испытания
Твердость Роквелла (R-Scale)110ASTM D785
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 2(3.18 mm)1920MPaASTM D638
Прочность на растяжение 3(3.18 mm)40.7MPaASTM D638
Удлинение при растяжении 4(Break, 3.18 mm)6.0%ASTM D638
Флекторный модуль 51930MPaASTM D790
Flexural Strength 667.6MPaASTM D790
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Зубчатый изод Impact (23°C)200J/mASTM D256A
Незубчатый изод Impact (23°C)480J/mASTM D256
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура отклонения при нагрузке ASTM D648
    0.45 MPa, Unannealed 110°C
    1.8 MPa, Unannealed 96.1°C
Температура перехода стекла 125°CDMA
Викат Температура размягчения 112°CASTM D1525
CLTE- Поток 7.4E-5cm/cm/°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Диэлектрическая прочность 3.5 to 13kV/mmASTM D149
Диэлектрическая постоянная 72.70 to 2.90ASTM D150
Коэффициент рассеивания 83.2E-3 to 3.5E-3ASTM D150
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость HBUL 94
Примечание
1 .All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation.
2 .Type I, 5.1 mm/min
3 .Type I, 5.1 mm/min
4 .Type I, 5.1 mm/min
5 .Method I (3 point load), 1.3 mm/min
6 .Method I (3 point load), 1.3 mm/min
7 .All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation.
8 .All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation.
Тип материала Категория Производитель
Niblend AE/V0 AF HT PC+ABS Soredi S.p.a.
Multilon® MK-1000A PC+ABS TEIJIN LIMITED
EMERGE™ PC/ABS 7570EP PC+ABS Trinseo
LUBEMIX 85 BLACK PC+ABS LUBEN PLAST srl
PermaStat® 2500 PC+ABS RTP Company
CYCOLOY™ C3650 resin PC+ABS SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами