Описание материалов:
Bayfill 382 is a semi-rigid polyurethane foam system designed for automotive interior applications. The Bayfill 382 system is an excellent choice for the production of soft-touch panels, such as instrument panels, door trim, and center consoles. The foam is typically molded in a back-filling process between a soft, exterior skin and a rigid, thermoplastic substrate.
The Bayfill 382 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a polyol mixture. As with any product, use of the Bayfill 382 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Используется | - Пена
- Применение в автомобильной области
- Автомобильные внутренние детали
- Оборудование для салона автомобиля
- Приборная панель автомобиля
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Литая плотность | 143 | kg/m³ | ASTM D3574A |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Отклонение силы сжатия | | | ASTM D3574C |
| -- 1 | 0.276 | MPa | ASTM D3574C |
| -- 2 | 0.200 | MPa | ASTM D3574C |
| Комплект сжатия | | | ASTM D3574D |
| Cd 3 | 66 | % | ASTM D3574D |
| Cd 4 | 54 | % | ASTM D3574D |
| Ct 5 | 27 | % | ASTM D3574D |
| Ct 6 | 33 | % | ASTM D3574D |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| -- 7 | 0.386 | MPa | ASTM D3574K |
| -- | 0.510 | MPa | ASTM D3574E |
| Удлинение при растяжении | | | |
| Fracture 8 | 23 | % | ASTM D3574K |
| Fracture | 31 | % | ASTM D3574E |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength | 0.350 | kN/m | ASTM D3574F |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта | | | |
| Component a | Mixing ratio by weight: 53 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Dark brown to black liquid
Specific Gravity @ 25°C: 1.24
Viscosity @25°C: 200 cps
Flash Point PMCC: 199°C
NCO: 31 wt%
Part B
Type: Polyol
Appearance: Black liquid
Specific Gravity @ 25°C: 1.01
Viscosity @25°C: 1400 cps
Flash Point PMCC: 131°C
Water: 2.8 wt%
Hydroxyl Number: 70 KOH/g
Material Temperatures: 27 to 32°CMold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C
Cream Time: 14 to 22 sec
Top of Cup Time: 50 to 64 sec
Gel Time: 60 to 76 sec
Rise Time: 87 to 107 sec
Free-Rise Density: 2.9 to 4.5 lb/ft³
Machine Reactivity at 29°C
Cream Time: 8 to 12 sec
Top of Cup Time: 24 to 30 sec
Gel Time: 40 to 45 sec
Rise Time: 60 to 65 sec
Free-Rise Density: 3.10 to 4.10 lb/ft³
Molded Density: 8.0 to 11.0 lb/ft³ |
| Примечание |
|---|
| 1 . | 0.5 |
| 2 . | After J2 Autoclave |
| 3 . | After J2 Autoclave, Cd=compression set as a percentage of the original deflection |
| 4 . | 50, Cd=compression set as a percentage of the original deflection |
| 5 . | 50%, Ct=compression set as a percentage of the original thickness |
| 6 . | After J2 Autoclave, Ct=compression set as a percentage of the original thickness |
| 7 . | Dry Heat Aged at 140°C |
| 8 . | Dry Heat Aged at 140°C |