Описание материалов:
BC 9020 is a violet colored, two-component, flowable compound that, regardless of thickness or confinement, cures at room temperature. The cured rubber is high strength and high tear with good elongation. In addition, BC 9020 features low viscosity, low durometer, and resistance to sulfur clays. BC 9020 is a mold making material designed for the manufacture of flexible molds. These rubber molds are recommended for the use in repetitive production of intricate shapes cast from epoxy or urethane resins. These molds are also used in the potting of electronic components and in protecting sensitive assemblies against thermal shock and vibration.
| Главная Информация | |
|---|
| Характеристики | - Хорошая прочность на разрыв
- Высокое удлинение
- Высокая прочность
- Низкая вязкость
|
| Используется | - Электрическое/электронное применение
- Формы/штампы/инструменты
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.10 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 0.30 to 0.40 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 23 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | 4.14 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 500 | % | ASTM D638 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength | 21.0 | kN/m | ASTM D624 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта | | | |
| Hardener | Mix Ratio by Weight: 1.0 | | |
| Resin | Mix Ratio by Weight: 10 | | |
| Срок службы горшка (24°C) | 60 | min | |
| Срок годности (27°C) | 26 | wk | |
| Терморегулирующая вязкость (25°C) | 3.10E+6 | cP | ASTM D2393 |
| Время демолд (24°C) | 480 | min | |