LUVOCOM® 50-8779

Категория	PC, Polycarbonate
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	sOTp4R_LUVOCOM-50-8779.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®50-8779 is a polycarbonate (PC) material,. This product is available in Europe,.

LUVOCOM®The main features of 50-8779 are:

Conductivity

Good dimensional stability

Typical application areas include:

Electrical/electronic applications

engineering/industrial accessories

business/office supplies

Sporting goods

medical/health care

Главная Информация
Характеристики	Хорошая стабильность размеров Теплопроводность
Используется	Электрическое/электронное применение Инженерные аксессуары Бизнес-оборудование Спортивные товары Медицинские принадлежности/принадлежности для ухода
Внешний вид	Серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.39	g/cm³	ISO 1183
Формовочная усадка	0.40 - 0.70	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.20	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	10000	MPa	ISO 527-2
Tensile Stress (Break)	41.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	0.70	%	ISO 527-2
Флекторный модуль	8500	MPa	ISO 178
Флекторный стресс	62.0	MPa	ISO 178
Flexural Strain at Flexural Strength	1.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	7.0	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B
Теплопроводность ¹	17	W/m/K

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+3	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки	120	°C
Время сушки	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	280 - 300	°C
Средняя температура	290 - 310	°C
Передняя температура	300 - 320	°C
Температура сопла	290 - 310	°C
Температура обработки (расплава)	295	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Примечание
1 .	Hot-Disk, 60x60x3 mm

Тип материала	Категория	Производитель
RAMTOUGH RZ320G2/RZ321G2	PC	Polyram Ram-On Industries
QR Resin QR-1018-FR	PC	QTR, Inc.
STAR-THERM® E GN FR TS0	PC	EPIC Polymers
LEXAN™ MLS43R resin	PC	SABIC Innovative Plastics Asia Pacific
LNP™ LUBRICOMP™ DP001E compound	PC	SABIC Innovative Plastics
CALIBRE™ 5101-15	PC	Trinseo

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

