Monprene® SP-19985 XRD2 (PRELIMINARY DATA)
Описание материалов:
Monprene SP-19985 XRD2 is a high performance thermoplastic elastomer designed for a variety of consumer sporting goods applications including playground flooring requiring a soft, rubber-like feel. Monprene SP-19985 XRD2, available in NAT and colors, is a higher hardness, medium density, UV stabilized grade that exhibits excellent abrasion resistance and is suitable for injection molding.
| Главная Информация | |
|---|
| Характеристики | - Защита от солнечного света
- Гладкость
- Стабилизация света
- Хорошая устойчивость к ультрафиолетовому излучению
- Хорошая окраска
- Высокая яркость
- Устойчивость к абляции
- Смазка
- Заполнение
- Бромирование
- Высокая твердость
- Промежуточная плотность
- Огнестойкий
|
| Используется | - Напольный материал
- Замена резины
|
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.02 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shore A, 1 second, injection molding | 87 | | ASTM D2240 |
| Shore A, 5 seconds, injection molding | 85 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress 1 | | | ASTM D412 |
| Transverse flow
: 100% strain | 4.87 | MPa | ASTM D412 |
| Flow
: 100% strain | 5.77 | MPa | ASTM D412 |
| Transverse flow
: 300% strain | 6.32 | MPa | ASTM D412 |
| Flow
: 300% strain | 7.43 | MPa | ASTM D412 |
| Прочность на растяжение 2 | | | ASTM D412 |
| Transverse flow
: Fracture | 9.10 | MPa | ASTM D412 |
| Flow
: Fracture | 9.94 | MPa | ASTM D412 |
| Удлинение при растяжении 3 | | | ASTM D412 |
| Transverse flow
: Fracture | 600 | % | ASTM D412 |
| Flow
: Fracture | 550 | % | ASTM D412 |
| Tear Strength 4 | | | ASTM D624 |
| Transverse flow | 37.3 | kN/m | ASTM D624 |
| Flow | 44.8 | kN/m | ASTM D624 |
| Комплект сжатия 5 | | | ASTM D395B |
| 23°C, 22 hr | 40 | % | ASTM D395B |
| 70°C, 22 hr | 71 | % | ASTM D395B |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс кислорода | 20 | % | ASTM D2863 |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Задняя температура | 193 - 216 | °C | |
| Средняя температура | 193 - 216 | °C | |
| Передняя температура | 193 - 216 | °C | |
| Температура сопла | 193 - 216 | °C | |
| Температура обработки (расплава) | 193 - 216 | °C | |
| Температура формы | 16 - 32 | °C | |
| Давление впрыска | 1.38 - 6.89 | MPa | |
| Скорость впрыска | Moderate-Fast | | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Подушка | 3.81 - 25.4 | mm | |
| Инструкции по впрыску |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Примечание |
|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Type 1 |