Geon™ 210 Series 215 Blending Resin
Описание материалов:
Geon® 215 is a low molecular weight particle size homopolymer blending resin intended for use in plastisol formulations. It improves air release performance resulting in reduced scrap rates. It decreases high shear viscosity providing an improved 'ease of coating' performance resulting in a more uniform plastisol coating and improving line up time. It reduces viscosity aging characteristics, providing increased plastisol usage (pot life). It reduces surface gloss of films or coated products resulting in less surface blocking and improved handling.
Geon® 215 is recommended for solid and foamed plastisol applications such as coated fabric, cast films and coatings, foam mats and pads.
| Главная Информация | |
|---|
| Формы | |
| Метод обработки | - Прессформа слякоти
- Ротационное формование
- Литье
- Метод нанесения покрытия
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.40 | g/cm³ | ASTM D792 |
| K-Value 1 | 64.0 | | |
| Видимая свободная плотность 2 | 0.430 | g/cm³ | Internal method |
| Внутренняя вязкость | 0.85 | | ASTM D1243-60-A |
| Размер частиц | | | Internal method |
| < 52 Micron 3 | 98.0 | % | Internal method |
| < 74 Micron 4 | 99.8 | % | Internal method |
| Average Particle Size 5 | 25.0 | µm | Internal method |
| Relative Viscosity 6 | 2.12 | | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Дымка-
Плавленый 5 минут
(177 °C) 7 | 20 | % | Internal method |
| Блеск-
60 ° плавленый 5 минут
(177 °C) 8 | 20 | % | Internal method |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Вязкость брокфилда | | | Internal method |
| FF 9 | 4.00 | Pa·s | Internal method |
| Initial Viscosity @ 20 rpm 10 | 3.50 | Pa·s | Internal method |
| Initial Viscosity @ 2rpm 11 | 3.40 | Pa·s | Internal method |
| One Day Viscosity @ 20rpm 12 | 4.23 | Pa·s | Internal method |
| Отрежьте отток-
95 фунтов на квадратный дюйм 13 | 276.00 | g/10 min | Internal method |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Остаточный винилхлорид мономер 14 | | ppm | Internal method |
| Испарители 15 | 0.060 | % | Internal method |
| Процесс полимеризации | Suspension | | |
| Температура геля-
ПП 16 | 78 | °C | Internal method |
| Виниловый диффузор 17 | 75.0 | µm | Internal method |
| Note:The value set forth represent "typical" values and Mexichem Specialty Resins, therefore, makes no representation that the material in any particular shipment will conform to the listed properties.Packaging: This resin is shipped in multi-wall paper bags, net weight 50 lbs, 2500 lbs per pallet. Information shown on the package includes commercial identification number, lot and weight.Geon® ALTC (formulation): 60phr Geon® 121A, 40phr Geon® 215, 57phr DINP, 3phr ESO, and 2phr Therm-Chek SP 120 LOHFGeon® STP 1203(formulation): 60phr Geon® 178, 40phr Geon® 215,and 60phr DOP |
| Примечание |
|---|
| 1 . | Interrelationship |
| 2 . | Geon® STP 1169 |
| 3 . | <53 µ |
| 4 . | Geon® DFT 1466 |
| 5 . | Geon® 812 |
| 6 . | 1% Cyclohexanone |
| 7 . | 60, melting for 3 minutes, ALTC-65 |
| 8 . | 60, melt for 5 minutes, ALTC-65 |
| 9 . | Geon® ALTC 22 (with provided formulation) |
| 10 . | One day, V12,Geon®1010 |
| 11 . | Initial, V12,Geon®1010 |
| 12 . | Geon® ALTC 22 (with provided formulation) |
| 13 . | 95 psi |
| 14 . | Geon® STP 1005 |
| 15 . | Bags, Geon®793 |
| 16 . | Geon® ALTC 29 (with provided formulation) |
| 17 . | Geon® STP 1203 (with provided formulation) |