Описание материалов:

LUVOCOM®65-8722 is a polypropylene copolymer (PP Copoly) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 65-8722 are:

Conductivity

Good stiffness

chemical resistance

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал
Характеристики	Проводящий Жесткий, хороший Статическая проводимость Хорошая прочность Хорошая химическая стойкость
Внешний вид	Натуральный цвет
Формы	Частицы

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.32	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.30	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	11000	MPa	ISO 527-2
Tensile Stress (Break)	75.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	1.2	%	ISO 527-2
Флекторный модуль	12000	MPa	ISO 178
Флекторный стресс	115	MPa	ISO 178
Flexural Strain at Flexural Strength	1.8	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	130	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0E+4 - 1.0E+8	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	100	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+9	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки- Осушитель сушилка	70 - 95	°C
Время сушки- Осушитель сушилка	2.0 - 4.0	hr
Задняя температура	220 - 250	°C
Средняя температура	220 - 250	°C
Передняя температура	230 - 260	°C
Температура сопла	220 - 250	°C
Температура обработки (расплава)	230 - 260	°C
Температура формы	40 - 80	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
REPOL® H029SG	PP Homopolymer	Reliance Industries Limited
Lucent PP CPP-340	PP, Unspecified	Lucent Polymers, Inc.
PROTEQ™ C4Q6	PP Copolymer	Marplex Australia Pty. Ltd.
RheTech Polypropylene HP520-00	PP Copolymer	RheTech, Inc.
POLYfill PPH TS8030	PP Homopolymer	Polykemi AB
Hostacom EKC 330N E1 G12882	PP Copolymer	LyondellBasell Industries