LUVOCOM® 3-8896/WT/V-0

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	reDRaY_LUVOCOM38896WTV0.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®3-8896/WT/V-0 is a polyamide 6 (nylon 6) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 3-8896/WT/V-0 are:

Flame Retardant

Conductivity

Good stiffness

Typical application areas include:

Electrical/electronic applications

textile/fiber

engineering/industrial accessories

Automotive Industry

Главная Информация
Характеристики	Теплопроводность Жесткий, хороший Хорошая прочность Огнестойкий
Используется	Электрическое/электронное применение Текстильные изделия Инженерные аксессуары Применение в автомобильной области
Внешний вид	Белый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.78	g/cm³	ISO 1183
Формовочная усадка	0.70 - 0.90	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 1.3	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	5500	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.0	%	ISO 527-2
Флекторный модуль	4500	MPa	ISO 178
Флекторный стресс	80.0	MPa	ISO 178
Flexural Strain at Flexural Strength	2.6	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	130	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+13	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	28	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	90.0	°C	UL 746B
Теплопроводность ¹	1.2	W/m/K

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+13	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	75	°C
Hot air dryer, B	105	°C
Время сушки
Hot air dryer, A	10 - 16	hr
Hot air dryer, B	4.0 - 6.0	hr
Задняя температура	250 - 270	°C
Средняя температура	270 - 290	°C
Передняя температура	280 - 300	°C
Температура сопла	270 - 280	°C
Температура обработки (расплава)	270	°C
Температура формы	70 - 110	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Примечание
1 .	Hot-Disk, 60x60x3 mm

Тип материала	Категория	Производитель
SOLLAMID B 2720	Nylon 6	Krisoll Resinas Plásticas Ltda.
Tarnamid® T- 27 GF25 M	Nylon 6	Grupa Azoty S.A.
TUFNYL® SXXIC GRANITE GREY	Nylon 6	SRF Ltd.
Petlon Prime B1-G50-00-NT	Nylon 6	Petlon Polymers Ltd
Next Nylon 6 Industrial Series NGF30-02BK	Nylon 6	Next Polymers Ltd.
Akulon® K224-HG7	Nylon 6	DSM Engineering Plastics

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

