Описание материалов:
Monprene OM-16175 is a specialty thermoplastic elastomer designed for overmolding applications like grips and anti-skid parts for a variety of consumer and industrial products. Monprene OM-16175 is a medium hardness, low density opaque grade that is available in Black, Natural, and can be pre-colored, and exhibits excellent adhesion to nylon.
| Главная Информация | |
|---|
| Характеристики | - Гладкость
- Стабилизация света
- Сплоченность
- Хорошая окраска
- Хорошая адгезия
- Средняя степень жидкости
- Смазка
- Промежуточная плотность
- Средняя твердость
|
| Используется | - Ручка
- Формовочная форма для облицовки
- Электропитание/другие инструменты
- Мягкая ручка
- Мобильный телефон
- Спортивные товары
- Замена резины
- Ручка
- Склеивание
|
| Соответствие RoHS | |
| Внешний вид | - Неуказанный цвет
- Черный
- Натуральный цвет
|
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.958 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (200°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shore A, 1 second, injection molding | 77 | | ASTM D2240 |
| Shore A, 5 seconds, injection molding | 75 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress 1 | | | ASTM D412 |
| Transverse flow
: 100% strain | 2.55 | MPa | ASTM D412 |
| Flow
: 100% strain | 2.98 | MPa | ASTM D412 |
| Transverse flow
: 300% strain | 4.81 | MPa | ASTM D412 |
| Flow
: 300% strain | 5.85 | MPa | ASTM D412 |
| Прочность на растяжение 2 | | | ASTM D412 |
| Transverse flow
: Fracture | 8.23 | MPa | ASTM D412 |
| Flow
: Fracture | 7.51 | MPa | ASTM D412 |
| Удлинение при растяжении 3 | | | ASTM D412 |
| Transverse flow
: Fracture | 490 | % | ASTM D412 |
| Flow
: Fracture | 420 | % | ASTM D412 |
| Tear Strength 4 | | | ASTM D624 |
| Transverse flow | 37.7 | kN/m | ASTM D624 |
| Flow | 35.9 | kN/m | ASTM D624 |
| Комплект сжатия 5 | | | ASTM D395B |
| 23°C, 22 hr | 41 | % | ASTM D395B |
| 70°C, 22 hr | 76 | % | ASTM D395B |
| Дополнительная информация | Номинальное значение | | |
|---|
| Adhesion to Nylon | | | |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 60 | °C | |
| Время сушки | 2.0 - 4.0 | hr | |
| Задняя температура | 182 - 204 | °C | |
| Средняя температура | 182 - 204 | °C | |
| Передняя температура | 182 - 204 | °C | |
| Температура сопла | 182 - 204 | °C | |
| Температура обработки (расплава) | 182 - 204 | °C | |
| Температура формы | 16 - 32 | °C | |
| Давление впрыска | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Подушка | 3.81 - 25.4 | mm | |
| Инструкции по впрыску |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 2 to 4 hours at 140°F. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 171 - 193 | °C | |
| Зона цилиндра 2 температура. | 171 - 193 | °C | |
| Зона цилиндра 3 темп. | 171 - 193 | °C | |
| Зона цилиндра 4 темп. | 171 - 193 | °C | |
| Зона цилиндра 5 темп. | 171 - 193 | °C | |
| Температура матрицы | 171 - 193 | °C | |
| Примечание |
|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Type 1 |