Описание материалов:
Eastar™ GN007 Copolyester is a water-clear glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar™ GN007 copolyester will not crystallize and thus offers wider processing latitude than conventional crystallizable polyesters. This material offers an excellent combination of clarity, toughness, and melt strength that makes it useful for a variety of processing techniques and end-use applications.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая прочность расплава
- Хороший выпуск пресс-формы
- Хорошая технологичность
- Хорошая прочность
- Высокая четкость
|
| Используется | - Контейнеры
- Косметическая упаковка
- Мебель
- Товары для дома
- Персональный уход
- Спортивные товары
- Стационарные принадлежности
- Ручки зубной щетки
- Игрушки
- Инструменты для письма
|
| Внешний вид | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.27 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 108 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 23°C | 2030 | MPa | ASTM D638 |
| 23°C | 2000 | MPa | ISO 527-2 |
| Прочность на растяжение | | | |
| Yield, 23°C | 50.0 | MPa | ASTM D638 |
| Yield, 23°C | 48.0 | MPa | ISO 527-2 |
| Break, 23°C | 30.0 | MPa | ASTM D638 |
| Break, 23°C | 29.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C | 4.4 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 180 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 2060 | MPa | ASTM D790 |
| 23°C | 2100 | MPa | ISO 178 |
| Flexural Strength | | | |
| 23°C | 68.0 | MPa | ASTM D790 |
| 23°C | 67.0 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -40°C | 4.4 | kJ/m² | ISO 180 |
| 23°C | 9.4 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4218 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | °C | ASTM D648, ISO 75-2/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания (Total) | 90.0 | % | ASTM D1003 |
| Haze | 0.20 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.0 | °C | |
| Время сушки | 6.0 | hr | |
| Температура обработки (расплава) | 249 to 271 | °C | |
| Температура формы | 16.0 to 38.0 | °C | |