Описание материалов:
Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 74 | | ASTM D2240 |
| Shaw D | 25 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.276 | MPa | ASTM D695 |
| 5% strain | 0.655 | MPa | ASTM D695 |
| 10% strain | 1.34 | MPa | ASTM D695 |
| 15% strain | 2.00 | MPa | ASTM D695 |
| 20% strain | 3.21 | MPa | ASTM D695 |
| 25% strain | 4.00 | MPa | ASTM D695 |
| 50% strain | 8.96 | MPa | ASTM D695 |
| Устойчивость к истиранию | 11.7 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 3.62 | MPa | ASTM D412 |
| 300% strain | 7.41 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 46.9 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 550 | % | ASTM D412 |
| Комплект сжатия | 60 | % | ASTM D395 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 5.0 - 7.0 | min | |
| Время демолд | 60 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 435 pliAverage Split Tear, ASTM D1938: 185 pliStoichiometry Curative Level: 97%Break Set, ASTM D412-80: 8%NBS Abrasion: 205% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 7.96 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 8.02 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 8.09 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 8.15 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 8.21 parts by weightMix Temperature:
Andur M-22: 194-212°F
Curative DEG: 77-158°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 90.0 - 120 | °C | |