Описание материалов:
Bayflex 180 is a high-performance polymer system with excellent heat stability, low moisture absorption, low thermal expansion characteristics and excellent impact resistance. Parts made from this material have excellent surface and paint adhesion qualities and have a DOI (Distinction of Image) comparable to painted steel parts. A wide range of parts can be molded with the Bayflex 180 system, from thin wallstock rocker panels and trim to large, durable body panels and engine enclosures for specialty equipment. As with any product, use of the Bayflex 180 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
The Bayflex 180 system is supplied as two reactive liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer and Component B is a polyether polyol.
| Главная Информация | |
|---|
| Характеристики | - Низкая гигроскопичность
- Хорошая ударопрочность
- Распылитель
- Термическая стабильность, хорошая
- Отличный внешний вид
|
| Используется | - Детали под крышкой двигателя автомобиля
- Применение в автомобильной области
- Автомобильные внешние части
- Внешнее украшение автомобиля
|
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792, ASTM D1622 |
| Формовочная усадка-
Поток | 1.7 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, 3.18 mm) | 69 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 3.18 mm) | 28.3 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 3.18 mm) | 130 | % | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -30°C, 3.18 mm | 1460 | MPa | ASTM D790 |
| 23°C, 3.18 mm | 586 | MPa | ASTM D790 |
| 65°C, 3.18 mm | 434 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 3.18 mm) | 28.3 | MPa | ASTM D412 |
| Удлинение при растяжении (Break, 3.18 mm) | 130 | % | ASTM D412 |
| Tear Strength 1(3.18 mm) | 105 | kN/m | ASTM D624 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (3.18 mm) | 270 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток (3.18 mm) | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта 2 | | | |
| Component a | Mixing ratio by weight: 150 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Срок годности (32°C) | 26 | wk | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Sag 3 | | | ASTM D3769 |
| 4 in Overhang
: 121°C, 3.18 mm | 177.8 | µm | ASTM D3769 |
| 6 in Overhang
: 121°C, 3.18 mm | 7620.0 | µm | ASTM D3769 |
| Part A
Type: Isocyanate
Appearance: Colorless to light yellow liquid
Specific Gravity @ 25°C: 1.1
Viscosity @25°C: 735 mPa-s
Flash Point PMCC: >93 °C
Part B
Type: Polyol
Appearance: Yellow to amber liquid
Specific Gravity @ 25°C: 1.01
Viscosity @25°C: 960 mPa-s
Flash Point PMCC: 164 °C
Molding Parameters
Material Temperature: 32 to 43 °C
Mold Temperature: 71 to 74 °C
Typical Cure Time, 0.125 in: 30 sec
Polyol Nucleation - Specific Gravity: 0.70 to 0.75 0 |
| Примечание |
|---|
| 1 . | C mould |
| 2 . | 105 Index |
| 3 . | 1 hr |