Описание материалов:
Baydur 641 IBS is a rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system is supplied as two reactive liquid components and is typically used with a blowing paste purchased separately. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. The blowing paste is Baydur PU-1731.
The Baydur 641 IBS system is used in the industrial and medical equipment markets for applications requiring dimensional stability and excellent surface finish, such as, rollers for photographic and X-ray film processing equipment. As with any product, use of Baydur 641 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Хорошая стабильность размеров
- Отличный внешний вид
|
| Используется | - Структурная пена
- Промышленное применение
- Медицинские принадлежности/принадлежности для ухода
|
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.399 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток (12.7 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, 12.7 mm) | 50 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 12.7 mm) | 7.58 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 12.7 mm) | 8.0 | % | ASTM D638 |
| Флекторный модуль (12.7 mm) | 372 | MPa | ASTM D790 |
| Flexural Strength (12.7 mm) | 14.5 | MPa | ASTM D790 |
| Прочность на сжатие (12.7 mm) | 6.21 | MPa | ASTM D695 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength 1 | 7.1 | kJ/m² | Internal method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (0.45 MPa, unannealed, 12.7mm) | 65.0 | °C | ASTM D648 |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта | | | |
| Component a | Mixing ratio by weight: 110 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Dark brown liquid
Specific Gravity @ 25°C: 1.24
Viscosity @25°C: 200 cps
Flash Point PMCC: 199°C
NCO: 31.5 wt%
Part B
Type: Polyol
Appearance: Pale yellow liquid
Specific Gravity @ 25°C: 1.02
Viscosity @25°C: 2000 cps
Flash Point PMCC: 187°C
Water: 0.45 wt%
Hydroxyl Number: 367 KOH/g
Material Temperatures: 27 to 35°CMold Temperature: 60 to 70°CHand Mix Reactivity at 25°C
Cream Time: 8 to 13 sec
Gel Time: 15 to 25 sec
Tack Free Time: 23 to 28 sec
Free-Rise Density: 7.5 to 10 lb/ft³
Polyol Nucleation Specific Gravity: 0.85 to 0.90 0Typical cure Time, 0.500 in Thickness: 4 sec |