LUVOCOM® 1105-7786 VP

Категория PEEK, Polyetheretherketone
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF qTe3MN_LUVOCOM-1105-7786-VP.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1105-7786 VP is a polyetheretherketone (PEEK) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main characteristics of 1105-7786 VP are:
  • flame retardant/rated flame
  • Flame Retardant
  • anti-warping
  • chemical resistance
  • Wear-resistant

Typical application areas include:
  • engineering/industrial accessories
  • textile/fiber
  • Aerospace
  • Automotive Industry
  • Handle
Главная Информация
Добавка
  • Ptfe лубрикант
Характеристики
  • Низкий уровень защиты
  • Хорошая химическая стойкость
  • Хорошая стойкость к истиранию
  • Сопротивление гидролизу
  • Смазка
  • Огнестойкий
Используется
  • Ручка
  • Текстильные изделия
  • Инженерные аксессуары
  • Аэрокосмическое применение
  • Машина/механические детали
  • Применение в автомобильной области
  • Медицинские принадлежности/принадлежности для ухода
  • Подшипник
Внешний вид
  • Черный
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.35g/cm³ISO 1183
Плавкий объем-расход (MVR) (380°C/10.0 kg)16.0cm³/10minISO 1133
Формовочная усадка 1.0 - 1.8%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.050%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 3600MPaISO 527-2
Tensile Stress (Break)90.0MPaISO 527-2
Растяжимое напряжение (Yield)5.0%ISO 527-2
Флекторный модуль 3000MPaISO 178
Флекторный стресс 130MPaISO 178
Flexural Strain at Flexural Strength 6.5%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 260°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance > 1.0E+12ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Ударная прочность (23°C)5.0kJ/m²ISO 179/1eA
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 250°CUL 746B
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость 1V-0UL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    Hot air dryer, A 150°C
    Hot air dryer, B 120°C
Время сушки
    Hot air dryer, A 3.0 - 6.0hr
    Hot air dryer, B 6.0 - 8.0hr
Рекомендуемая максимальная влажность 0.050%
Задняя температура 360 - 370°C
Средняя температура 380 - 390°C
Передняя температура 390 - 400°C
Температура сопла 360 - 380°C
Температура обработки (расплава) 390°C
Температура формы 170 - 190°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Примечание
1 .Not recognized by UL.
Тип материала Категория Производитель
DynaPath™ 3265-E PEEK Polymer Dynamix
Edgetek™ PK-000/000 EM Natural PEEK PolyOne Corporation
LNP™ THERMOCOMP™ LF002XXP-WT02005 compound PEEK SABIC Innovative Plastics Europe
AKROTEK® PEEK GF 60 9 natural (5184) PEEK AKRO-PLASTIC GmbH
LUVOCOM® 1105-8161 PEEK Lehmann & Voss & Co.
LUVOCOM® 1105-8167 PEEK Lehmann & Voss & Co.
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами