Описание материалов:
HWF-852B is a certified prime grade Hexene copolymer HIGH MOLECULAR WEIGHT developed for production of thin gauged high stiffness paper-like Blown films. HWF-852B features BIMODAL-BROAD molecular weight distribution that greatly improves processability in HDPE equipment, outstanding film mechanical properties, and high drawdown film capability. HWF-852B applications include shoppers, grocery bags, merchant and produce bags, refuse sacks, single and multiwall liners, lamination films, meat & cheese wrap films, and as substitute films for grease-proof waxed and acid free papers. Minimum recommended film gauge is 0.4 mil, and processing temperature 210 to 230°C. HWF-852B complies with FDA regulation 21CFR 177.1520 (c) 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Высокая Молекулярная масса
- Сополимер
- Гексен-комномер
- Обрабатываемость, хорошая
- Хорошее Отшелушивание
- Соответствие пищевого контакта
- Бимодульное молекулярное распределение веса
|
| Используется | - Пленка
- Ламинат
- Подкладка
- Сумка
- Пищевая упаковка
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.952 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/2.16 kg | 0.050 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 8.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 10 | µm | |
| Толщина пленки-рекомендовано/доступно | Minimum 10 µm (0.4 mil) | | |
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD | 790 | MPa | ASTM D882 |
| 1% secant, TD | 965 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield | 28.0 | MPa | ASTM D882 |
| TD
: Yield | 26.0 | MPa | ASTM D882 |
| MD
: Fracture | 69.0 | MPa | ASTM D882 |
| TD
: Fracture | 41.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Fracture | 330 | % | ASTM D882 |
| TD
: Fracture | 480 | % | ASTM D882 |
| Ударное падение Dart 1 | 280 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD | 20 | g | ASTM D1922 |
| TD | 200 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура плавления | 129 | °C | ASTM D3417 |
| Дополнительная информация |
|---|
| Film Specimen: 0.4 mil (10 µm) film, melt temperature 410-440°F (210-225°C), blow-up-ratio 4.0:1, frost line height 8 x die ø. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 210 - 230 | °C | |