Viton® A-100
| Категория | FKM, Fluoroelastomer , Fluorelastomer |
| Производитель | DuPont Performance Elastomers |
| Торговая марка | Viton® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
ottyRK_Viton-A-100.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Viton A-100 fluoroelastomer is an ultralow-viscosity, "A-type" gum polymer that demonstrates improved processing and rheology in comparison with existing fluoroelastomers. Viton A-100 is especially designed for use with Viton Curative #50. It may be blended with other Viton types to enhance flow and processibility.
Compared with other "A-family" dipolymers, Viton A-100 provides:
-Ultralow viscosity
-Improved processing
-increased mold flow
-can be blended with other Viton types to enhance processibility and improve flow
-Excellent mold release
-Good compression set resistance for low-viscosity types of Viton
Applications
-Transfer and injection molding of complex shapes such as gaskets
-Extrusions
--can be used to modify viscosity of other types of Viton
-Solution coating
--fabric
--tanks or chemical containers
Compared with other "A-family" dipolymers, Viton A-100 provides:
-Ultralow viscosity
-Improved processing
-increased mold flow
-can be blended with other Viton types to enhance processibility and improve flow
-Excellent mold release
-Good compression set resistance for low-viscosity types of Viton
Applications
-Transfer and injection molding of complex shapes such as gaskets
-Extrusions
--can be used to modify viscosity of other types of Viton
-Solution coating
--fabric
--tanks or chemical containers
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 1.82 | g/cm³ | ASTM D792 |
| Вязкость Mooney (ML 1+10, 121°C) | 33 | MU | ASTM D1646 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Твердость дюрометра (Shore A) | 79 | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress (100% Strain) | 3.80 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 8.20 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 240 | % | ASTM D412 |
| Комплект сжатия | |||
| 23°C, 70 hr | 10 | % | ASTM D395B |
| 200°C, 70 hr | 21 | % | ASTM D395 |
| 232°C, 22 hr | 23 | % | ASTM D395B |
| Старение | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Изменение прочности на растяжение в воздухе | ASTM D573 | ||
| 200°C, 70 hr | 43 | % | ASTM D573 |
| 100% strain, 200°C, 70 hr | 110 | % | ASTM D573 |
| 200°C, 168 hr | 45 | % | ASTM D573 |
| 100% strain, 200°C, 168 hr | 100 | % | ASTM D573 |
| 232°C, 24 hr | 30 | % | ASTM D573 |
| 100% strain, 232°C, 24 hr | 45 | % | ASTM D573 |
| 232°C, 70 hr | 41 | % | ASTM D573 |
| 100% strain, 232°C, 70 hr | 110 | % | ASTM D573 |
| Изменение максимального удлинения в воздухе | ASTM D573 | ||
| 200°C, 70 hr | -36 | % | ASTM D573 |
| 200°C, 168 hr | -35 | % | ASTM D573 |
| 232°C, 24 hr | -24 | % | ASTM D573 |
| 232°C, 70 hr | -37 | % | ASTM D573 |
| Изменение твердости дюрометра в воздухе | ASTM D573 | ||
| Support a, 200°C, 70 hr | 1.0 | ASTM D573 | |
| Support a, 200°C, 168 hr | 2.0 | ASTM D573 | |
| Support a, 232°C, 24 hr | 4.0 | ASTM D573 | |
| Support a, 232°C, 70 hr | 4.0 | ASTM D573 |
| Дополнительная информация |
|---|
| Mooney Scorch, MS at 121°C, Minimum: 17 in-lbMooney Scorch, MS at 121°C, 2-pt rise: >30 minODR at 177°C, Microdie, 3° Arc, 15 min, ML: 2 in-lbODR at 177°C, Microdie, 3° Arc, 15 min, ts2: 2.7 minODR at 177°C, Microdie, 3° Arc, 15 min, tc90: 4.1 minODR at 177°C, Microdie, 3° Arc, 15 min, Mc90: 83 in-lbODR at 177°C, Microdie, 3° Arc, 15 min, MH: 92 in-lbRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 12.7 mm/min, 113 s^-1: 4.0 MPaRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 50.8 mm/min, 452 s^-1: 6.8 MPaRosand Capillary Rheometer, 100°C, 1.5 mm Die, L/D=0/1, 127 mm/min, 1130 s^-1: 9.9 MPaNominal Viscosity, ML 1 + 10, 121°C: 10Polymer Fluorine Content: 66% |
| Тип материала | Категория | Производитель |
|---|---|---|
| Viton® ETP-600S | Fluorelastomer | DuPont Performance Elastomers |
| Tecnoflon® T 538 | Fluorelastomer | Solvay Specialty Polymers |
| Boda BDF361P | Fluorelastomer | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Cri-Line GP-715-OR | Fluorelastomer | Cri-Tech, Inc. |
| Cri-Line LC-915-LV | Fluorelastomer | Cri-Tech, Inc. |
| Jiangsu Meilan XXMLF2-13W | Fluorelastomer | Jiangsu Meilan Chemical Co., Ltd. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved